DuPont Performance Polymers Zytel® 70G33HS1L NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G33HS1L NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
33% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G33HS1L NC010 is a 33% glass fiber reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
DAM; ISO 1183
Water Absorption 5.7 %

@Thickness 2.00 mm
 5.7 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.80 %

@Thickness 2.00 mm
 1.80 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Water Absorption at Saturation 1.2 %
1.2 %
DAM; Immersion 24h; ASTM D570
Viscosity 198170 cP

@Shear Rate 500 1/s,
Temperature 295 °C
 198170 cP

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
Viscosity Test 130 cm³/g
130 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
50%RH; ISO 527-1/-2
200 MPa
29000 psi
DAM; ISO 527-1/-2
Tensile Stress 13.24 MPa

@Strain 0.300 %,
Temperature 150 °C
 1920 psi

@Strain 0.300 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
20.91 MPa

@Strain 0.200 %,
Temperature 23.0 °C
 3033 psi

@Strain 0.200 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
21.792 MPa

@Strain 0.500 %,
Temperature 150 °C
 3160.7 psi

@Strain 0.500 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
32.13 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 4660 psi

@Strain 0.500 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
35.04 MPa

@Strain 0.900 %,
Temperature 150 °C
 5082 psi

@Strain 0.900 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
45.024 MPa

@Strain 1.30 %,
Temperature 150 °C
 6530.2 psi

@Strain 1.30 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
45.7 MPa

@Strain 0.400 %,
Temperature 0.000 °C
 6630 psi

@Strain 0.400 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
45.82 MPa

@Strain 0.400 %,
Temperature -40.0 °C
 6646 psi

@Strain 0.400 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
49.8 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 7220 psi

@Strain 0.500 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
50.11 MPa

@Strain 1.50 %,
Temperature 150 °C
 7268 psi

@Strain 1.50 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
52.73 MPa

@Strain 0.600 %,
Temperature 0.000 °C
 7648 psi

@Strain 0.600 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
57.312 MPa

@Strain 1.90 %,
Temperature 150 °C
 8312.4 psi

@Strain 1.90 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
61.4 MPa

@Strain 2.10 %,
Temperature 150 °C
 8910 psi

@Strain 2.10 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
65.7 MPa

@Strain 0.600 %,
Temperature -40.0 °C
 9530 psi

@Strain 0.600 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
65.952 MPa

@Strain 2.50 %,
Temperature 150 °C
 9565.5 psi

@Strain 2.50 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
71.19 MPa

@Strain 1.30 %,
Temperature 23.0 °C
 10330 psi

@Strain 1.30 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
75.89 MPa

@Strain 0.800 %,
Temperature 23.0 °C
 11010 psi

@Strain 0.800 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
76.75 MPa

@Strain 0.700 %,
Temperature 0.000 °C
 11130 psi

@Strain 0.700 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
77.0 MPa

@Strain 0.700 %,
Temperature -40.0 °C
 11200 psi

@Strain 0.700 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
77.82 MPa

@Strain 0.900 %,
Temperature 0.000 °C
 11290 psi

@Strain 0.900 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
81.76 MPa

@Strain 4.50 %,
Temperature 150 °C
 11860 psi

@Strain 4.50 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
92.34 MPa

@Strain 1.90 %,
Temperature 23.0 °C
 13390 psi

@Strain 1.90 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
98.36 MPa

@Strain 1.20 %,
Temperature 0.000 °C
 14270 psi

@Strain 1.20 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
106.06 MPa

@Strain 1.00 %,
Temperature 0.000 °C
 15383 psi

@Strain 1.00 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
106.62 MPa

@Strain 1.00 %,
Temperature -40.0 °C
 15464 psi

@Strain 1.00 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
109.17 MPa

@Strain 2.50 %,
Temperature 23.0 °C
 15834 psi

@Strain 2.50 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
121.5 MPa

@Strain 1.40 %,
Temperature 23.0 °C
 17620 psi

@Strain 1.40 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
123.11 MPa

@Strain 1.60 %,
Temperature 0.000 °C
 17856 psi

@Strain 1.60 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
131.98 MPa

@Strain 1.30 %,
Temperature 0.000 °C
 19142 psi

@Strain 1.30 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
136.23 MPa

@Strain 1.30 %,
Temperature -40.0 °C
 19759 psi

@Strain 1.30 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
147.5 MPa

@Strain 1.50 %,
Temperature -40.0 °C
 21390 psi

@Strain 1.50 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
176.3 MPa

@Strain 1.90 %,
Temperature -40.0 °C
 25570 psi

@Strain 1.90 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
179.66 MPa

@Strain 3.40 %,
Temperature 0.000 °C
 26058 psi

@Strain 3.40 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
199.09 MPa

@Strain 3.20 %,
Temperature 23.0 °C
 28876 psi

@Strain 3.20 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
212.5 MPa

@Strain 2.50 %,
Temperature -40.0 °C
 30820 psi

@Strain 2.50 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
224.79 MPa

@Strain 3.00 %,
Temperature 0.000 °C
 32603 psi

@Strain 3.00 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
251.95 MPa

@Strain 2.90 %,
Temperature -40.0 °C
 36542 psi

@Strain 2.90 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
Elongation at Break 3.5 %
3.5 %
DAM; ISO 527-1/-2
5.0 %
5.0 %
50%RH; ISO 527-1/-2
Tensile Modulus 8.00 GPa
1160 ksi
50%RH; ISO 527-1/-2
10.5 GPa
1520 ksi
DAM; ISO 527-1/-2
Flexural Strength 200 MPa
29000 psi
50%RH; ISO 178
290 MPa
42100 psi
DAM; ISO 178
Flexural Modulus 6.21 GPa
901 ksi
50%RH; ISO 178
9.30 GPa
1350 ksi
DAM; ISO 178
Shear Strength 0.099085 MPa

@Shear Rate 500 1/s,
Temperature 295 °C
 14.371 psi

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
Secant Modulus 2.34 GPa

@Strain 3.70 %,
Temperature 100 °C
 339 ksi

@Strain 3.70 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
2.67 GPa

@Strain 3.70 %,
Temperature 100 °C
 387 ksi

@Strain 3.70 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
2.74 GPa

@Strain 3.40 %,
Temperature 80.0 °C
 398 ksi

@Strain 3.40 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
2.80 GPa

@Strain 2.90 %,
Temperature 100 °C
 406 ksi

@Strain 2.90 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
2.91 GPa

@Strain 3.80 %,
Temperature 80.0 °C
 422 ksi

@Strain 3.80 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
3.24 GPa

@Strain 2.60 %,
Temperature 80.0 °C
 470 ksi

@Strain 2.60 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2
3.2868 GPa

@Strain 2.50 %,
Temperature 100 °C
 476.72 ksi

@Strain 2.50 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
3.30 GPa

@Strain 2.10 %,
Temperature 100 °C
 479 ksi

@Strain 2.10 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
3.42 GPa

@Strain 3.70 %,
Temperature 23.0 °C
 495 ksi

@Strain 3.70 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
3.72 GPa

@Strain 2.40 %,
Temperature 80.0 °C
 539 ksi

@Strain 2.40 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
3.77 GPa

@Strain 1.80 %,
Temperature 80.0 °C
 546 ksi

@Strain 1.80 %,
Temperature 176 °F
 50%RH; ISO 11403-1 -2