Eastman D4052-F Polyethylene  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman D4052-F Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
D4052-F is a fractional-melt low density formulation with low slip and low antiblock. It is suggested for film applications requiring impact strength, outstanding clarity, and good tear resistance. This product is suggested for packaging frozen foods and for similar applications requiring toughness and clarity.Information from manufacturer data sheet.Eastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ASTM D4883
Moisture Vapor Transmission 18.6 cc-mm/m²-24hr-atm
47.2 cc-mil/100 in²-24hr-atm
ASTM F372
Oxygen Transmission 200 cc-mm/m²-24hr-atm
508 cc-mil/100 in²-24hr-atm
ASTM D1434
Thickness 38.0 microns
1.50 mil
Melt Flow 0.70 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.70 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 33.0 MPa
4790 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 200 %
200 %
ASTM D882
Film Elongation at Break, TD 800 %
800 %
ASTM D882
Secant Modulus, MD 0.220 GPa
31.9 ksi
1% Secant; ASTM D882
Secant Modulus, TD 0.274 GPa
39.7 ksi
1% Secant; ASTM D882
Coefficient of Friction 0.20
0.20
ASTM D1894
Elmendorf Tear Strength MD 550 g
550 g
Elmendorf Tear Strength TD 130 g
130 g
Elmendorf Tear Strength, MD 14.5 g/micron
368 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.40 g/micron
86.4 g/mil
ASTM D1922
Dart Drop 2.90 g/micron
73.7 g/mil
ASTM D1709A
Film Tensile Strength at Break, MD 33.0 MPa
4790 psi
ASTM D882
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 95.0 °C
203 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
ASTM D1003
Gloss 70 %
70 %
at 45°; ASTM D2457
Transmission, Visible 90 %
90 %
ASTM D1746
Descriptive Properties Value Comments
Process Film