ExxonMobil LDPE LD 160AT Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 160AT Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 160 series are LDPE grades, which offer good draw down and optical properties.Availability: Africa & Middle East, Asia Pacific, Latin America, North America and South America Additive: Antiblock: 1200 ppmSlip: 900 ppmThermal Stabilizer: YesApplications: Cast FilmHigh Clarity FilmLaundry FilmProduce BagsProfile ExtrusionZipper Bag Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
ExxonMobil method
Melt Flow 4.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 1200 ppm
1200 ppm
Slip Level 900 ppm
900 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.3 MPa
1500 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.3 MPa
1500 psi
ASTM D882
Film Elongation at Break, MD 220 %
220 %
ASTM D882
Film Elongation at Break, TD 450 %
450 %
ASTM D882
Elmendorf Tear Strength MD 170 g
170 g
ASTM D1922
Elmendorf Tear Strength TD 130 g
130 g
ASTM D1922
Dart Drop Test 70.0 g
0.154 lb
ASTM D1709A
Film Tensile Strength at Break, MD 19.3 MPa
2800 psi
ASTM D882
Film Tensile Strength at Break, TD 15.2 MPa
2200 psi
ASTM D882
1% Secant Modulus, MD 179 MPa
26000 psi
ASTM D882
1% Secant Modulus, TD 207 MPa
30000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 226 °C
<= 439 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 5.4 %
5.4 %
ASTM D1003
Gloss 70 %
70 %
45°; ASTM D2457