ExxonMobil LLDPE LL 1002X75 Linear Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Exxon Chemical
Trade Name LLDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LLDPE LL 1002X75 Linear Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LL 1002 resins are butane LLDPE designed for the blown film process. Films made form LL 1002 resins have very good tensile and toughness properties. LL 1002.09 is a granular material which, while it can be used for film production, is also suitable for compounding.Availability: Latin America, North America and South America Additive: Antiblock: 7500 ppmSlip: 1350 ppmProcessing Aid: NoThermal Stabilizer: YesApplications: Agricultural FilmBag in BoxBlown FilmCast FilmFood packagingForm Fill and Seal PackagingFreezer FilmGarment FilmGeneral PackagingIndustrial Packaging LinersMulch FilmPackaging FilmsProduce Bags on a Roll Shoppers Trash Can LinersInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ExxonMobil method
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 7500 ppm
7500 ppm
Slip Level 1350 ppm
1350 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.27 MPa
1200 psi
ASTM D882
Film Tensile Strength at Yield, TD 8.27 MPa
1200 psi
ASTM D882
Film Elongation at Break, MD 660 %
660 %
ASTM D882
Film Elongation at Break, TD 780 %
780 %
ASTM D882
Puncture Energy 1.10 J
0.808 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 120 g
120 g
ASTM D1922
Elmendorf Tear Strength TD 340 g
340 g
ASTM D1922
Dart Drop Test 70.0 g
0.154 lb
ASTM D1709A
Film Tensile Strength at Break, MD 36.5 MPa
5300 psi
ASTM D882
Film Tensile Strength at Break, TD 26.2 MPa
3800 psi
ASTM D882
1% Secant Modulus, MD 179 MPa
26000 psi
ASTM D882
1% Secant Modulus, TD 193 MPa
28000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 253 °C
<= 487 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 29 %
29 %
ASTM D1003
Gloss 22 %
22 %
45°; ASTM D2457