- Ineos ABS Triax® 1185 ABS/Nylon Alloy, Injection Molding Grade
Ineos ABS Triax® 1185 ABS/Nylon Alloy, Injection Molding Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Triax® 1185 ABS/Nylon Alloy, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Triax® 1185 resin is an ABS (Acrylonitrile Butadiene Styrene)/Nylon 6 alloy for injection molding. It is a semicrystalline thermoplastic with excellent processability, good chemical resistance, good fatigue performance, and excellent abrasion characteristics. Triax® 1185 resin has excellent impact resistance across a broad temperature range and excellent surface appearance. Triax® 1185 resin is designed for use in large parts requiring a smooth finish and consistent appearance. Typical applications include components for recreational vehicles, snowmobiles, sporting goods, and a variety of parts for industrial and consumer applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM-D792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM-D792 |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 230 °C |
20 g/10 min @Load 22.0 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527 |
| Tensile Modulus | 1.40 GPa | 203 ksi | ISO 527 |
| Flexural Strength | 45.0 MPa | 6530 psi | ISO 178 |
| Flexural Modulus | 1.15 GPa | 167 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 28.0 kJ/m² @Temperature -40.0 °C |
13.3 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 57.0 kJ/m² @Temperature -30.0 °C |
27.1 ft-lb/in² @Temperature -22.0 °F |
ISO 180 | |
| 81.0 kJ/m² @Temperature 23.0 °C |
38.5 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Impact Test | 20.0 J @Temperature 23.0 °C |
14.8 ft-lb @Temperature 73.4 °F |
Multiaxial Impact; E-max; 0.100 in. thickness, 1.57 in. ring, 0.5 in. dart, 3.46 m/s velocity |
| 24.0 J @Temperature -30.0 °C |
17.7 ft-lb @Temperature -22.0 °F |
Multiaxial Impact; E-max; 0.100 in. thickness, 1.57 in. ring, 0.5 in. dart, 3.46 m/s velocity | |
| 40.0 J @Temperature 23.0 °C |
29.5 ft-lb @Temperature 73.4 °F |
Multiaxial Impact; E-fail; 0.100 in. thickness, 1.57 in. ring, 0.5 in. dart, 3.46 m/s velocity | |
| 44.0 J @Temperature -30.0 °C |
32.5 ft-lb @Temperature -22.0 °F |
Multiaxial Impact; E-fail; 0.100 in. thickness, 1.57 in. ring, 0.5 in. dart, 3.46 m/s velocity |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75 |
| Vicat Softening Point | 190 °C | 374 °F | A/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 266 °C | 450 - 511 °F | Injection Molding |
| Middle Barrel Temperature | 232 - 266 °C | 450 - 511 °F | Injection Molding |
| Front Barrel Temperature | 232 - 266 °C | 450 - 511 °F | Injection Molding |
| Nozzle Temperature | 249 - 260 °C | 480 - 500 °F | Injection Molding |
| Melt Temperature | 238 - 271 °C | 460 - 520 °F | Injection Molding |
| Mold Temperature | 38.0 - 93.0 °C | 100 - 199 °F | Injection Molding |
| Drying Temperature | 88.0 °C @Time 7200 - 14400 sec |
190 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | 0.15 - 0.35 % | 0.15 - 0.35 % | |
| Dew Point | <= -29.0 °C | <= -20.2 °F | inlet air |
| Injection Pressure | 41.4 - 82.7 MPa | 6000 - 12000 psi | Injection Molding |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | Injection Molding |
| Clamp Pressure | 46.2 - 77.0 MPa | 6700 - 11200 psi | Injection Molding |
| Cushion | <= 0.317 cm | <= 0.125 in | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Hold Pressure | 30-50% of Injection Pressure, Injection Molding | |
| Injection Speed | Fast | Injection Molding |
| Screw Compression Ratio | 2.5:1 | Injection Molding |
| Screw Length-to-Diameter Ratio | >= 20:1 | Injection Molding |
| Screw Speed | Moderate, Injection Molding | |
| Shot Weight-to-Machine Capacity Ratio | 0.5-0.7 | Injection Molding |