Kingfa PBT-T30 30% Mineral Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Mineral Filled
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa PBT-T30 30% Mineral Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Excellent size stabilityLow tendency to wrapLow abrasionGood surfaceApplications:Injection moldingApplication partsE & E partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc

@Temperature 23.0 °C
1.50 g/cc

@Temperature 73.4 °F
ASTM D792
Water Absorption 0.060 %

@Temperature 23.0 °C,
Time 86400 sec
0.060 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm

@Temperature 23.0 °C
0.0060 - 0.0080 in/in

@Temperature 73.4 °F
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM D785
Tensile Strength at Break 47.0 MPa
6820 psi
10mm/min; ASTM D638
Elongation at Break 8.0 %
8.0 %
10mm/min; ASTM D638
Flexural Strength 90.0 MPa
13100 psi
2mm/min; ASTM D790
Flexural Modulus 3.50 GPa
508 ksi
2mm/min; ASTM D790
Izod Impact, Notched 0.480 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
0.899 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 205 °C

@Thickness 6.40 mm
401 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 115 °C

@Thickness 6.40 mm
239 °F

@Thickness 0.252 in
ASTM D648
Flammability, UL94 HB

@Thickness 1.50 - 1.65 mm
HB

@Thickness 0.0591 - 0.0650 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Processing Temperature <= 280 °C
<= 536 °F
Rear Barrel Temperature 220 - 240 °C
428 - 464 °F
Start Point: 230°C
Middle Barrel Temperature 230 - 250 °C
446 - 482 °F
Start Point: 240°C
Front Barrel Temperature 240 - 260 °C
464 - 500 °F
Start Point: 250°C
Melt Temperature 240 - 260 °C
464 - 500 °F
Start Point: 250°C
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Start Point: 60°C
Drying Temperature 120 - 140 °C

@Time 10800 - 18000 sec
248 - 284 °F

@Time 3.00 - 5.00 hour
Pre-dry
Descriptive Properties Value Comments
Injection Speed Moderate to High
Mineral Content (%) 30