Overview of materials for Nylon 610, Carbon Fiber Filled

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Carbon Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 610, Carbon Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 610, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.04 - 1.44 g/cc
0.0375 - 0.0520 lb/in³
Average value: 1.24 g/cc Grade Count:15
Filler Content 15.0 - 40.0 %
15.0 - 40.0 %
Average value: 25.6 % Grade Count:8
Water Absorption 0.120 - 0.300 %
0.120 - 0.300 %
Average value: 0.192 % Grade Count:10
Linear Mold Shrinkage 0.00100 - 0.0160 cm/cm
0.00100 - 0.0160 in/in
Average value: 0.00409 cm/cm Grade Count:15
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 31.4 - 234 MPa
4560 - 34000 psi
Average value: 150 MPa Grade Count:15
Elongation at Break 1.50 - 10.0 %
1.50 - 10.0 %
Average value: 3.36 % Grade Count:12
Modulus of Elasticity 2.30 - 27.6 GPa
333 - 4000 ksi
Average value: 13.0 GPa Grade Count:13
Flexural Yield Strength 89.6 - 372 MPa
13000 - 54000 psi
Average value: 249 MPa Grade Count:13
Flexural Modulus 2.76 - 22.1 GPa
400 - 3200 ksi
Average value: 12.5 GPa Grade Count:13
Izod Impact, Notched 0.366 - 1.60 J/cm
0.685 - 3.00 ft-lb/in
Average value: 0.940 J/cm Grade Count:14
Izod Impact, Unnotched 3.79 - 10.7 J/cm
7.10 - 20.0 ft-lb/in
Average value: 7.37 J/cm Grade Count:10
Charpy Impact Unnotched 6.00 - 6.00 J/cm²

@Temperature -30.0 - -30.0 °C
28.6 - 28.6 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 6.00 J/cm² Grade Count:1
Charpy Impact, Notched 1.00 - 1.00 J/cm²

@Temperature -30.0 - -30.0 °C
4.76 - 4.76 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 1.00 J/cm² Grade Count:1
Thermal Properties Metric English Comments
CTE, linear 14.4 - 16.2 µm/m-°C
8.00 - 9.00 µin/in-°F
Average value: 15.5 µm/m-°C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 216 - 232 °C
420 - 450 °F
Average value: 222 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi) 98.9 - 227 °C
210 - 440 °F
Average value: 201 °C Grade Count:13
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:10
Electrical Properties Metric English Comments
Electrical Resistivity 5.00 - 1.00e+14 ohm-cm
5.00 - 1.00e+14 ohm-cm
Average value: 1.11e+13 ohm-cm Grade Count:10
Processing Properties Metric English Comments
Processing Temperature 265 - 293 °C
509 - 560 °F
Average value: 282 °C Grade Count:9
Melt Temperature 240 - 299 °C
464 - 570 °F
Average value: 276 °C Grade Count:4
Mold Temperature 65.6 - 107 °C
150 - 225 °F
Average value: 87.6 °C Grade Count:12
Drying Temperature 75.0 - 105 °C
167 - 221 °F
Average value: 84.7 °C Grade Count:4
Moisture Content 0.170 - 1.20 %
0.170 - 1.20 %
Average value: 0.523 % Grade Count:3
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi
Average value: 96.5 MPa Grade Count:9