Overview of materials for Nylon 66/Nylon 6 Blend, Glass Fiber Filled

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/Nylon 6 Blend, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66/Nylon 6 Blend, Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/Nylon 6 Blend, Glass Fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.18 - 1.58 g/cc
0.0426 - 0.0571 lb/in³
Average value: 1.35 g/cc Grade Count:14
1.24 - 1.24 g/cc

@Temperature 295 - 295 °C
0.0448 - 0.0448 lb/in³

@Temperature 563 - 563 °F
Average value: 1.24 g/cc Grade Count:1
Water Absorption 1.20 - 6.80 %
1.20 - 6.80 %
Average value: 3.80 % Grade Count:8
Moisture Absorption at Equilibrium 1.70 - 2.70 %
1.70 - 2.70 %
Average value: 2.17 % Grade Count:4
Linear Mold Shrinkage 0.00100 - 0.0140 cm/cm
0.00100 - 0.0140 in/in
Average value: 0.00631 cm/cm Grade Count:12
Linear Mold Shrinkage, Transverse 0.00560 - 0.0140 cm/cm
0.00560 - 0.0140 in/in
Average value: 0.00853 cm/cm Grade Count:3
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 80.0 - 230 MPa
11600 - 33400 psi
Average value: 141 MPa Grade Count:12
Elongation at Break 2.40 - 16.0 %
2.40 - 16.0 %
Average value: 5.03 % Grade Count:13
Modulus of Elasticity 3.40 - 17.0 GPa
493 - 2470 ksi
Average value: 8.25 GPa Grade Count:10
0.654 - 10.89 GPa

@Temperature -20.0 - 250 °C
94.9 - 1579 ksi

@Temperature -4.00 - 482 °F
Average value: 4.47 GPa Grade Count:2
Flexural Yield Strength 120 - 240 MPa
17400 - 34800 psi
Average value: 189 MPa Grade Count:6
Flexural Modulus 3.30 - 10.0 GPa
479 - 1450 ksi
Average value: 6.65 GPa Grade Count:11
Izod Impact, Notched 0.900 - 1.50 J/cm
1.69 - 2.81 ft-lb/in
Average value: 1.18 J/cm Grade Count:4
Izod Impact, Notched (ISO) 5.00 - 23.0 kJ/m²
2.38 - 10.9 ft-lb/in²
Average value: 13.9 kJ/m² Grade Count:5
11.0 - 15.0 kJ/m²

@Temperature -40.0 - -40.0 °C
5.23 - 7.14 ft-lb/in²

@Temperature -40.0 - -40.0 °F
Average value: 12.8 kJ/m² Grade Count:3
Charpy Impact Unnotched 4.50 - 11.5 J/cm²
21.4 - 54.7 ft-lb/in²
Average value: 8.23 J/cm² Grade Count:7
4.00 - 9.00 J/cm²

@Temperature -30.0 - -20.0 °C
19.0 - 42.8 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 7.25 J/cm² Grade Count:6
Charpy Impact, Notched 0.550 - 4.00 J/cm²
2.62 - 19.0 ft-lb/in²
Average value: 1.64 J/cm² Grade Count:8
0.300 - 1.50 J/cm²

@Temperature -40.0 - -20.0 °C
1.43 - 7.14 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 1.01 J/cm² Grade Count:8
Thermal Properties Metric English Comments
CTE, linear 14.0 - 47.0 µm/m-°C
7.78 - 26.1 µin/in-°F
Average value: 23.4 µm/m-°C Grade Count:5
CTE, linear, Transverse to Flow 75.0 - 120 µm/m-°C
41.7 - 66.7 µin/in-°F
Average value: 97.0 µm/m-°C Grade Count:4
Melting Point 235 - 263 °C
455 - 505 °F
Average value: 254 °C Grade Count:9
Deflection Temperature at 0.46 MPa (66 psi) 225 - 255 °C
437 - 491 °F
Average value: 245 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi) 200 - 250 °C
392 - 482 °F
Average value: 224 °C Grade Count:14
Vicat Softening Point 225 - 255 °C
437 - 491 °F
Average value: 240 °C Grade Count:4
Flammability, UL94 HB
HB
Grade Count:7
Processing Properties Metric English Comments
Melt Temperature 250 - 310 °C
482 - 590 °F
Average value: 287 °C Grade Count:9
Mold Temperature 70.0 - 120 °C
158 - 248 °F
Average value: 93.9 °C Grade Count:9
Drying Temperature 79.4 - 80.0 °C
175 - 176 °F
Average value: 79.9 °C Grade Count:9
Moisture Content 0.0500 - 0.200 %
0.0500 - 0.200 %
Average value: 0.177 % Grade Count:9
Injection Pressure 34.5 - 138 MPa
5000 - 20000 psi
Average value: 89.1 MPa Grade Count:3