Overview of materials for PVC, Transparent

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Transparent
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for PVC, Transparent.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PVC, Transparent". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.801 - 1.36 g/cc
0.0289 - 0.0491 lb/in³
Average value: 1.22 g/cc Grade Count:123
Apparent Bulk Density 0.540 - 0.780 g/cc
0.0195 - 0.0282 lb/in³
Average value: 0.618 g/cc Grade Count:5
Viscosity Test 90.0 - 125 cm³/g
90.0 - 125 cm³/g
Average value: 101 cm³/g Grade Count:5
Linear Mold Shrinkage 0.00200 - 0.0310 cm/cm
0.00200 - 0.0310 in/in
Average value: 0.0134 cm/cm Grade Count:12
Spiral Flow 63.5 - 102 cm
25.0 - 40.2 in
Average value: 78.8 cm Grade Count:5
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100 - 124
100 - 124
Average value: 110 Grade Count:3
Hardness, Shore A 33.0 - 110
33.0 - 110
Average value: 73.7 Grade Count:128
Hardness, Shore D 40.0 - 85.0
40.0 - 85.0
Average value: 72.2 Grade Count:20
Tensile Strength, Ultimate 6.29 - 42.7 MPa
912 - 6200 psi
Average value: 16.7 MPa Grade Count:112
Tensile Strength, Yield 1.79 - 60.1 MPa
260 - 8710 psi
Average value: 18.5 MPa Grade Count:49
Elongation at Break 19.0 - 520 %
19.0 - 520 %
Average value: 336 % Grade Count:118
Modulus of Elasticity 0.00552 - 3.17 GPa
0.801 - 460 ksi
Average value: 2.14 GPa Grade Count:13
Flexural Yield Strength 75.8 - 96.9 MPa
11000 - 14100 psi
Average value: 85.1 MPa Grade Count:12
Flexural Modulus 2.28 - 3.03 GPa
331 - 439 ksi
Average value: 2.81 GPa Grade Count:12
Izod Impact, Notched 0.427 - 10.6 J/cm
0.800 - 19.9 ft-lb/in
Average value: 3.59 J/cm Grade Count:12
0.534 - 1.07 J/cm

@Temperature 0.000 - 0.000 °C
1.00 - 2.00 ft-lb/in

@Temperature 32.0 - 32.0 °F
Average value: 0.668 J/cm Grade Count:4
0.534 - 1.07 J/cm

@Thickness 3.18 - 3.18 mm
1.00 - 2.00 ft-lb/in

@Thickness 0.125 - 0.125 in
Average value: 0.668 J/cm Grade Count:4
Tear Strength 29.8 - 114 kN/m
170 - 650 pli
Average value: 67.6 kN/m Grade Count:16
Compression Set 20.0 - 42.0 %
20.0 - 42.0 %
Average value: 30.4 % Grade Count:7
Clash Berg Modulus 0.00689 - 0.996 GPa
0.999 - 144 ksi
Average value: 0.477 GPa Grade Count:10
0.310 - 0.310 GPa

@Temperature -58.0 - -13.0 °C
45.0 - 45.0 ksi

@Temperature -72.4 - 8.60 °F
Average value: 0.310 GPa Grade Count:11
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 65.0 - 72.8 °C
149 - 163 °F
Average value: 68.7 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi) 61.1 - 76.7 °C
142 - 170 °F
Average value: 67.1 °C Grade Count:11
Brittleness Temperature -57.8 - 8.00 °C
-72.0 - 46.4 °F
Average value: -30.7 °C Grade Count:78
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:14
Optical Properties Metric English Comments
Haze 2.50 - 8.00 %
2.50 - 8.00 %
Average value: 4.52 % Grade Count:10
Transmission, Visible 70.0 - 90.0 %
70.0 - 90.0 %
Average value: 88.5 % Grade Count:115
Processing Properties Metric English Comments
Processing Temperature 199 - 213 °C
390 - 415 °F
Average value: 207 °C Grade Count:3
Melt Temperature 160 - 207 °C
320 - 405 °F
Average value: 188 °C Grade Count:25