Plastcom SLOVALEN PH 71 T 20 PP, 20% mineral filling

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVALEN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVALEN PH 71 T 20 PP, 20% mineral filling.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. General application in all industry branches. Delivered in natural mode and in the full RAL colour scale.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
Linear Mold Shrinkage 0.0083 cm/cm
0.0083 in/in
Linear Mold Shrinkage, Transverse 0.0072 cm/cm
0.0072 in/in
Melt Flow 17 g/10 min

@Load 0.325 kg,
Temperature 270 °C
17 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 31.0 MPa
4500 psi
Elongation at Break 6.0 %
6.0 %
Tensile Modulus 2.75 GPa
399 ksi
Flexural Strength 45.0 MPa
6530 psi
Flexural Modulus 2.60 GPa
377 ksi
Charpy Impact Unnotched 1.60 J/cm²

@Temperature -20.0 °C
7.61 ft-lb/in²

@Temperature -4.00 °F
3.60 J/cm²

@Temperature 23.0 °C
17.1 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.150 J/cm²

@Temperature -20.0 °C
0.714 ft-lb/in²

@Temperature -4.00 °F
0.300 J/cm²

@Temperature 23.0 °C
1.43 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 155 - 165 °C
311 - 329 °F
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
Vicat Softening Point 160 °C
320 °F
B
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Drying Temperature 70.0 °C
158 °F
Dry Time 2 hour
2 hour
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi