SABIC Innovative Plastics ULTEM CRS5311 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM CRS5311 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. Resin is RoHS compliant. UL94 V0 and 5VA listing.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.90 %
0.90 %
ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 360 °C
7.0 g/10 min

@Load 11.0 lb,
Temperature 680 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 165 MPa
23900 psi
ISO 2039-1
Tensile Strength at Break 160 MPa
23200 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 10.0 GPa
1450 ksi
1 mm/min; ISO 527
Flexural Strength 210 MPa
30500 psi
2 mm/min; ISO 178
Flexural Modulus 8.20 GPa
1190 ksi
2 mm/min; ISO 178
Izod Impact, Unnotched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
80*10*4; ISO 180/1U
35.0 kJ/m²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 23.0 - 150 °C
11.1 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 23.0 - 150 °C
38.9 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
Thermal Conductivity 0.330 W/m-K
2.29 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 220 °C
428 °F
Rate B/120; ISO 306
228 °C
442 °F
Rate A/50; ISO 306
Glass Transition Temp, Tg 225 °C
437 °F
UL RTI, Electrical 105 °C
221 °F
UL 746B
UL RTI, Mechanical with Impact 105 °C
221 °F
UL 746B
UL RTI, Mechanical without Impact 105 °C
221 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VA

@Thickness 1.50 mm
5VA

@Thickness 0.0591 in
UL 94
Glow Wire Test 960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
3.1

@Frequency 1.00e+6 Hz
IEC 60250
3.2

@Frequency 50.0 - 60.0 Hz
3.2

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 18.0 kV/mm

@Thickness 3.20 mm
457 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0020

@Frequency 50.0 - 60.0 Hz
0.0020

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0030

@Frequency 1.00e+6 Hz
0.0030

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index >= 100 V
>= 100 V
IEC 60112
150 V
150 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2