SABIC Innovative Plastics Xenoy® 6620 PBT+PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® 6620 PBT+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT+PC, Unreinforced, impact modified thermoplastic alloy. Outstanding impact at low temperature
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Water Absorption 0.080 %

@Time 86400 sec
 0.080 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.016 - 0.018 cm/cm

@Thickness 3.20 mm
 0.016 - 0.018 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.016 - 0.018 cm/cm

@Thickness 3.20 mm
 0.016 - 0.018 in/in

@Thickness 0.126 in
 SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
ASTM D785
Tensile Strength, Yield 43.0 MPa
6240 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 175 %
175 %
Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 64.0 MPa
9280 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.72 GPa
249 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 8.97 J/cm
16.8 ft-lb/in
ASTM D256
6.67 J/cm

@Temperature -30.0 °C
 12.5 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 16.02 J/cm
30.01 ft-lb/in
ASTM D4812
Gardner Impact 54.0 J
39.8 ft-lb
ASTM D3029
54.0 J
39.8 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 94.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 52.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
103 µm/m-°C

@Temperature 60.0 - 138 °C
 57.2 µin/in-°F

@Temperature 140 - 280 °F
 ASTM E 831
CTE, linear, Transverse to Flow 98.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 54.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C

@Thickness 3.20 mm
 199 °F

@Thickness 0.126 in
 unannealed; ASTM D648
98.0 °C

@Thickness 6.40 mm
 208 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C

@Thickness 3.20 mm
 127 °F

@Thickness 0.126 in
 unannealed; ASTM D648
60.0 °C

@Thickness 6.40 mm
 140 °F

@Thickness 0.252 in
 unannealed; ASTM D648
UL RTI, Electrical 75.0 °C
167 °F
UL 746B
UL RTI, Mechanical with Impact 75.0 °C
167 °F
UL 746B
UL RTI, Mechanical without Impact 75.0 °C
167 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.47 mm
 HB

@Thickness 0.0579 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 5.50e+16 ohm-cm
5.50e+16 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 100000 Hz
 3.0

@Frequency 100000 Hz
 ASTM D150
3.0

@Frequency 1.00e+6 Hz
 3.0

@Frequency 1.00e+6 Hz
 ASTM D150
3.1

@Frequency 100 Hz
 3.1

@Frequency 100 Hz
 ASTM D150
Dielectric Strength 19.0 kV/mm

@Thickness 3.20 mm
 483 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
19.0 kV/mm

@Thickness 3.20 mm
 483 kV/in

@Thickness 0.126 in
 in air; ASTM D149
27.9 kV/mm

@Thickness 1.60 mm
 709 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
Dissipation Factor 0.0020

@Frequency 100 Hz
 0.0020

@Frequency 100 Hz
 ASTM D150
0.020

@Frequency 100000 Hz
 0.020

@Frequency 100000 Hz
 ASTM D150
0.020

@Frequency 1.00e+6 Hz
 0.020

@Frequency 1.00e+6 Hz
 ASTM D150
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index >= 600 V
>= 600 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 10.0 - 25.4 mm/min
0.394 - 1.00 in/min
UL 746A
Descriptive Properties Value Comments
Specific Volume 0.83cm^3/g
ASTM D792