Solvay Specialty Polymers Kalix® 5950 HFFR Polyamide, High Performance (HPPA), 50% Glass Fiber

Category Polymer , Thermoplastic , Nylon
Manufacturer Solvay Specialty Polymers
Trade Name Kalix®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Kalix® 5950 HFFR Polyamide, High Performance (HPPA), 50% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Kalix® 5950 HFFR is a halogen-free, flame retardant (UL-94 V0 at 0.4 mm), highly reinforced polyamide material specifically formulated for high strength and stiffness applications where good impact resistance and excellent dimensional stability after molding are required. The formulation also addresses warpage issues associated with the anisotropic shrinkage of glass fiber reinforced materials so that close tolerance molding is more easily achieved. Its low viscosity and excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry.Features: Flame Retardant; Good Dimensional Stability; Good Impact Resistance; Good Surface Finish; Halogen Free; High Flow; High Stiffness; High Strength; Low Moisture Absorption; Low Warpage; Paintable; PlatableUses: Cell Phones; Electrical Parts; Electrical/Electronic Applications; Thin-walled PartsInjection Molding Notes: Kalix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Kalix® resins be dried prior to molding.Additional Properties: Flexural Strain at Break - ISO 178 2.2 %; Tensile Modulus - ISO 527-2 19700 MPa; Tensile Strain at Break - ISO 527-2 1.7 %; Tensile Strength - ISO 527-2 183 MPaInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ISO 1183
Filler Content 50 %
50 %
Glass Fiber
Water Absorption 0.11 %

@Time 86400 sec
0.11 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00060 cm/cm
0.00060 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0018 cm/cm
0.0018 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 245 MPa
35500 psi
ISO 527-2
Elongation at Break 1.8 %
1.8 %
ISO 527-2
Tensile Modulus 20.0 GPa
2900 ksi
ISO 527-2
Flexural Strength 350 MPa
50800 psi
ISO 178
Flexural Modulus 19.0 GPa
2760 ksi
ISO 178
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
Type 1, Notch A; ISO 180
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
HDT B; Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 247 °C
477 °F
Unannealed; ISO 75-2/A
Glass Transition Temp, Tg 40.0 °C
104 °F
DSC
Flammability, UL94 V-0

@Thickness 0.400 mm
V-0

@Thickness 0.0157 in
5VA

@Thickness 1.50 mm
5VA

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Dielectric Constant 4.48

@Frequency 2.40e+9 Hz
4.48

@Frequency 2.40e+9 Hz
ASTM D2520
Dissipation Factor 0.011

@Frequency 2.40e+9 Hz
0.011

@Frequency 2.40e+9 Hz
Method B; ASTM D2520
Processing Properties Metric English Comments
Rear Barrel Temperature 270 °C
518 °F
Front Barrel Temperature 300 °C
572 °F
Melt Temperature 280 - 285 °C
536 - 545 °F
Mold Temperature 115 - 130 °C
239 - 266 °F
Drying Temperature 80.0 °C

@Time 14400 - 43200 sec
176 °F

@Time 4.00 - 12.0 hour
Moisture Content <= 0.070 %
<= 0.070 %
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; White
Form Pellets
Part Marking Code >PAX6/MXD6-GF50<
ISO 11469
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant