- Toyobo VYLOPET® EMC130-20 Injection Molding Polyester Resin, Flame Resistant
Toyobo VYLOPET® EMC130-20 Injection Molding Polyester Resin, Flame Resistant
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo VYLOPET® EMC130-20 Injection Molding Polyester Resin, Flame Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Relay partsFeatures: Excellent arc resistanceFlame resistanceInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.91 g/cc | 0.0690 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | MD |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Strength | 150 MPa | 21800 psi | ASTM D790 |
| Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
| Izod Impact, Notched | 0.630 J/cm | 1.18 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 38 | 38 | CS-17; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C @Temperature 20.0 °C |
13.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 255 °C | 491 °F | By DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Thermal index; ASTM UL746B |
| 225 °C | 437 °F | Ball pressure temperature; IEC Method | |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.7937 mm |
V-0 @Thickness 0.03125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 24.0 kV/mm @Thickness 2.00 mm |
610 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 181 sec | 181 sec | UL recognition value, tungsten electrode; ASTM D495 |
| Comparative Tracking Index | 250 - 399 V | 250 - 399 V | IEC Pub1.112, class 2; IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F |
Users viewing this material also viewed the following:
- Malvern Minerals Novakup® 325 Surface-Treated Lamellar Quartz Filler/Extender
- Indium Corp. 16-2212 Flux Thinner
- Ipiranga Petrochem GM 7746 A HDPE
- Saint-Gobain CHR® K104 Polyimide Film Backing Silicone Adhesive Pressure Sensitive Tape
- Samsung Cheil Industries Starex® LX-0951 ABS, Unreinforced Metallic-Look
- Eagle Brass 706 Copper Nickel 10%, Hard
- Eastman Eastar MN004 Copolyester
- Diamond Polymers DIAMALOY 1418 Polycarbonate/Polyester Alloy
- Dow Corning 193C Fluid
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR Fumed Silica - Wacker HK N20
Copyright © lookpolymers.com All Rights Reserved