Unitika AX-1500W Dry

Category	Polymer , Thermoplastic , Polyarylate
Manufacturer	Unitika
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Unitika AX-1500W Dry.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics: A resin succeeding the advantages of AX1500 resin and containing titanium oxide at high concentration. Improved drastically in light reflection and blocking properties, aimed at display devices Chemical resistanceInformation provided by Unitika Ltd.

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ASTM D792
Water Absorption	0.72 % @Thickness 3.17 mm, Time 86400 sec	0.72 % @Thickness 0.125 in, Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Thickness 3.00 mm	0.0090 in/in @Thickness 0.118 in

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength at Break	79.0 MPa	11500 psi	ASTM D638
Elongation at Break	4.7 %	4.7 %	ASTM D638
Flexural Strength	125 MPa	18100 psi	ASTM D790
Flexural Modulus	3.50 GPa	508 ksi	ASTM D790
Izod Impact, Notched	0.430 J/cm @Thickness 3.17 mm	0.806 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	73.0 µm/m-°C	40.6 µin/in-°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	150 °C	302 °F	ASTM D648

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	200 - 220 °C	392 - 428 °F
Middle Barrel Temperature	220 - 240 °C	428 - 464 °F
Front Barrel Temperature	230 - 250 °C	446 - 482 °F
Nozzle Temperature	230 - 250 °C	446 - 482 °F
Mold Temperature	40.0 - 60.0 °C	104 - 140 °F	actual surface temp
Drying Temperature	100 °C	212 °F
Dry Time	10.0 - 24.0 hour	10.0 - 24.0 hour
Back Pressure	0.490 - 1.47 MPa	71.1 - 213 psi	gage pressure