Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 10.0 - 11.0 GPa | 1450 - 1600 ksi | ASTM D790 |
Prodways PLASTCure Rigid 10 500 3D Printing Polymer Superior thermo-mechanical properties.Suitable for the manufacture of parts that require thermal stability, extreme accuracy and quick turnaround. Exceptional for parts that are designed for wind tu.. |
|||
Flexural Modulus | 8.00 - 11.0 GPa | 1160 - 1600 ksi | Compression; ISO 178 |
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi.. |
|||
Flexural Modulus | 9.00 - 11.0 GPa | 1310 - 1600 ksi | Injection; ISO 178 |
Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve.. |
|||
Flexural Modulus | 9.00 - 11.0 GPa | 1310 - 1600 ksi | Compression; ISO 178 |
Raschig Group MELOPAS® 156 MF Melamine Glass fiber reinforced Melamine molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 200.. |
|||
Flexural Modulus | 1.57 - 11.0 GPa | 228 - 1600 ksi | Average value: 5.37 GPa Grade Count:127 |
Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an.. |
|||
Flexural Modulus | 0.00800 - 11.0 GPa | 1.16 - 1600 ksi | Average value: 8.29 GPa Grade Count:234 |
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25.. |
|||
Flexural Modulus | 4.80 - 11.0 GPa | 696 - 1600 ksi | Average value: 8.55 GPa Grade Count:5 |
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled". Each property range of values reported i.. |
|||
Flexural Modulus | 2.07 - 11.0 GPa | 300 - 1600 ksi | Average value: 3.68 GPa Grade Count:7 |
Overview of materials for Polyphenylene Ether, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, PTFE Filled". Each property range of values reported is minimum and maximum values .. |
|||
Flexural Modulus | 4.80 - 11.0 GPa | 696 - 1600 ksi | Average value: 7.41 GPa Grade Count:17 |
Overview of materials for Phenolic, Novolac, Cellulose Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Cellulose Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Flexural Modulus | 7.00 - 11.0 GPa | 1020 - 1600 ksi | Average value: 9.38 GPa Grade Count:8 |
Overview of materials for Phenolic, Novolac, Fabric Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Fabric Filled". Each property range of values reported is minimum and maximum values .. |
|||
Flexural Modulus | 8.96 - 11.0 GPa | 1300 - 1600 ksi | ASTM D790 |
Mar-Bal MB1000-PC Thermoset Polyester Composite Molding Compound A general purpose material that is easily customized. Designed for Powder Coating and Electrostatic painting.Mar-Bal standard grades can be injection, compression and transfer molded.Information pro.. |
|||
Flexural Modulus | 8.96 - 11.0 GPa | 1300 - 1600 ksi | ASTM D790 |
Mar-Bal MB2000-10 Thermoset Polyester Composite Molding Compound An excellent flame and track resistant material with excellent electrical and mechanical properties. Good dielectric strength and low shrink for close dimensional control.Mar-Bal standard grades can.. |
|||
Flexural Modulus | 8.96 - 11.0 GPa | 1300 - 1600 ksi | ASTM D790 |
Mar-Bal MB2000-5 Thermoset Polyester Composite Molding Compound An excellent flame and track resistant material with excellent electrical and mechanical properties. Good dielectric strength and low shrink for close dimensional control.Mar-Bal standard grades can.. |
|||
Flexural Modulus | 9.65 - 11.0 GPa | 1400 - 1600 ksi | ASTM D790 |
Mar-Bal MB3000-15 Thermoset Polyester Composite Molding Compound A superior chemical resistant material with excellent flame and track resistance.Mar-Bal standard grades can be injection, compression and transfer molded.Information provided by Mar-Bal, Inc. |
|||
Flexural Modulus | 9.00 - 11.0 GPa | 1310 - 1600 ksi | ISO 178 |
Vyncolit X681 Novolac Phenolic Glass fiber filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction. Tribological compound with PTFE additive.USES: Water pump seals and self-lubrica.. |
|||
Flexural Modulus | 9.65 - 11.0 GPa | 1400 - 1600 ksi | |
Bulk Molding Compounds BMC 1454 for Injection Molding Circuit Breakers BMC 1454 is a special low-cost material developed specifically for injection molding circuit breakers. It has considerable flame, arc and track resistance. BMC 1454 is a medium strength material wit.. |
|||
Flexural Modulus | 9.65 - 11.0 GPa | 1400 - 1600 ksi | |
Bulk Molding Compounds BMC A20-(a) High Strength Grade Molding Compound BMC A20 is a high strength, low shrink general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC A20 is well suited for injection, transfer or compression molding o.. |
|||
Flexural Modulus | 1.38 - 11.0 GPa | 200 - 1600 ksi | Average value: 3.70 GPa Grade Count:107 |
Overview of materials for Nylon 66, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, PTFE Filled". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Flexural Modulus | 2.34 - 11.0 GPa | 340 - 1600 ksi | Average value: 5.09 GPa Grade Count:11 |
Overview of materials for Acrylic/Polycarbonate Alloy, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Acrylic/Polycarbonate Alloy, Glass Fiber Filler". Each property range of values reported is minimum and .. |
|||
Flexural Modulus | 1.72 - 11.0 GPa | 250 - 1600 ksi | Average value: 4.23 GPa Grade Count:28 |
Overview of materials for Polycarbonate/ABS Alloy, Antistat/Conductive This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, Antistat/Conductive". Each property range of values reported is minimum and max.. |
|||
Flexural Modulus | 9.50 - 11.0 GPa @Temperature 80.0 - 80.0 °C |
1380 - 1600 ksi @Temperature 176 - 176 °F |
Average value: 10.2 GPa Grade Count:4 |
Overview of materials for Polypropylene with 60% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 60% Glass Fiber Filler". Specific grades with glass content between 55% and 64% are i.. |
|||
Flexural Modulus | 0.134 - 11.0 GPa | 19.4 - 1600 ksi | Average value: 1.39 GPa Grade Count:816 |
Overview of materials for Polypropylene Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene Copolymer". Each property range of values reported is minimum and maximum values of approp.. |
|||
Flexural Modulus | 9.65 - 11.0 GPa | 1400 - 1600 ksi | |
Bulk Molding Compounds BMC T40(20) Die Casting Replacement Grade Molding Compound BMC T40(20) was formulated as a direct replacement for aluminum die casting applications. T40(20) is UL recognized. Excellent mechanical properties and dimensional control allow molded parts to ma.. |
|||
Flexural Modulus | 9.00 - 11.0 GPa | 1310 - 1600 ksi | ISO 178 |
Bulk Molding Compounds tetra-DUR F 4306 Bulk Molding Compound Mechanical high grade standard productTypical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion pr.. |