BASF Ultramid® A3EG3 15% Glass Filled PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® A3EG3 15% Glass Filled PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | dry; ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | beginning dry; ISO 62 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 145 cm³/g | 145 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM Data; MD |
| Melt Flow | 70 g/10 min @Load 5.00 kg, Temperature 275 °C |
70 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 5mm/min; ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 125 MPa | 18100 psi | ISO Data |
| Flexural Modulus | 4.00 GPa | 580 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 |
| Tensile Creep Modulus, 1000 hours | 2500 MPa | 363000 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | 10 K/min |
| 260 °C | 500 °F | ASTM Test |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 5.5 @Frequency 1.00e+6 Hz |
5.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.16 @Frequency 1.00e+6 Hz |
0.16 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.30 @Frequency 100 Hz |
0.30 @Frequency 100 Hz |
IEC 60250 | |
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| FDA | 21 CFR 177.1500 | |
| Form | Pellets | |
| Impact Modified | No | |
| NSF Std. 51 | Yes | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat |
Users viewing this material also viewed the following:
- Rotuba H3 Cellulose Acetate
- Shin-Etsu Silicones X-52-7042 Fluid
- SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK
- Eurotec® Tecodur® PB70 GR30 NL CA 01 PBT/PET 30% glass fiber reinforced
- E-Polymers TEKANATE® G7007 Extrusion Injection Molding Polycarbonate
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N220 Filler
- SMAC CABLE® 2519S-20-08 Damping Material
- Wall Colmonoy COLMONOY® 23A & 24 - Nickel Alloy With Tungsten Carbide
- Master Bond Supreme 3AN One Component, Heat Curing Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved