DuPont Performance Polymers Delrin® 300ATB BK000 Acetal Homopolymer (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer	DuPont Performance Polymers
Trade Name	Delrin®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® 300ATB BK000 Acetal Homopolymer (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Delrin® 300ATB BK000 is a filled, medium viscosity, toughened acetal homopolymer for injection molding. It is well suited for antistatic applications.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³	ISO 1183
Linear Mold Shrinkage	0.015 cm/cm @Diameter 4.00 mm	0.015 in/in @Diameter 0.157 in	Normal
	0.017 cm/cm @Diameter 4.00 mm	0.017 in/in @Diameter 0.157 in	Parallel
Melt Flow	2.3 g/10 min @Load 2.16 kg, Temperature 190 °C	2.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	50.0 MPa @Temperature 23.0 °C	7250 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	16 % @Temperature 23.0 °C	16 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	2.30 GPa @Temperature 23.0 °C	334 ksi @Temperature 73.4 °F	ISO 527
Flexural Modulus	2.10 GPa @Temperature 23.0 °C	305 ksi @Temperature 73.4 °F	ISO 178
Izod Impact, Notched (ISO)	7.70 kJ/m² @Temperature 23.0 °C	3.66 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact, Notched	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	135 °C	275 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	70.0 °C	158 °F	ISO 75-1/-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	1e+05 @Temperature 23.0 °C	1e+05 @Temperature 73.4 °F	IEC 60093
Surface Resistance	1e+05 @Temperature 23.0 °C	1e+05 @Temperature 73.4 °F	IEC 60093

Processing Properties	Metric	English	Comments
Melt Temperature	205 °C	401 °F	Optimum; Injection Molding
	200 - 210 °C	392 - 410 °F	Injection Molding
Mold Temperature	90.0 °C	194 °F	optimum; Injection Molding
	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.050 %	<= 0.050 %	Injection Molding

Descriptive Properties	Value	Comments
Appearance	Black Color
Forms	Pellets
Generic	Acetal (POM) Homopolymer
Material Status	Preliminary Data
Polymer Family	POM
Polymer Type	POM Homopolymer
Processing Method	Injection Molding
Product Category	Static Dissipative Resins
	Toughened Resins
Region Available - Global	Yes
RoHS Compliance	Contact Manufacturer