DuPont Performance Polymers Zytel® HTN FR52G30NH NC010 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN FR52G30NH NC010 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide Zytel HTNFR52G30NH NC010 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin. It is also a PPA resin and it uses a non-halogenated flaInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
50%RH; ISO 527-1/-2
150 MPa
21800 psi
DAM; ISO 527-1/-2
Tensile Stress 9.87 MPa

@Strain 0.200 %,
Temperature 150 °C
 1430 psi

@Strain 0.200 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
11.62 MPa

@Strain 0.110 %,
Temperature 40.0 °C
 1685 psi

@Strain 0.110 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
12.69 MPa

@Strain 0.110 %,
Temperature -40.0 °C
 1841 psi

@Strain 0.110 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
13.04 MPa

@Strain 0.110 %,
Temperature 23.0 °C
 1891 psi

@Strain 0.110 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
13.14 MPa

@Strain 0.270 %,
Temperature 175 °C
 1906 psi

@Strain 0.270 %,
Temperature 347 °F
 DAM; ISO 11403-1 -2
13.72 MPa

@Strain 0.270 %,
Temperature 150 °C
 1990 psi

@Strain 0.270 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
17.16 MPa

@Strain 0.140 %,
Temperature 23.0 °C
 2489 psi

@Strain 0.140 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
19.61 MPa

@Strain 0.160 %,
Temperature -40.0 °C
 2844 psi

@Strain 0.160 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
31.31 MPa

@Strain 0.870 %,
Temperature 150 °C
 4541 psi

@Strain 0.870 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
34.48 MPa

@Strain 1.03 %,
Temperature 175 °C
 5001 psi

@Strain 1.03 %,
Temperature 347 °F
 DAM; ISO 11403-1 -2
36.87 MPa

@Strain 1.01 %,
Temperature 150 °C
 5348 psi

@Strain 1.01 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
43.17 MPa

@Strain 0.440 %,
Temperature 40.0 °C
 6261 psi

@Strain 0.440 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
43.52 MPa

@Strain 1.57 %,
Temperature 150 °C
 6312 psi

@Strain 1.57 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
46.16 MPa

@Strain 0.440 %,
Temperature 23.0 °C
 6695 psi

@Strain 0.440 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
46.47 MPa

@Strain 1.85 %,
Temperature 175 °C
 6740 psi

@Strain 1.85 %,
Temperature 347 °F
 DAM; ISO 11403-1 -2
49.45 MPa

@Strain 1.73 %,
Temperature 150 °C
 7172 psi

@Strain 1.73 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
50.65 MPa

@Strain 2.30 %,
Temperature 150 °C
 7346 psi

@Strain 2.30 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
52.7 MPa

@Strain 0.470 %,
Temperature -40.0 °C
 7640 psi

@Strain 0.470 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
52.78 MPa

@Strain 0.470 %,
Temperature 23.0 °C
 7655 psi

@Strain 0.470 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
53.31 MPa

@Strain 2.79 %,
Temperature 175 °C
 7732 psi

@Strain 2.79 %,
Temperature 347 °F
 DAM; ISO 11403-1 -2
58.12 MPa

@Strain 2.61 %,
Temperature 150 °C
 8430 psi

@Strain 2.61 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
59.93 MPa

@Strain 0.540 %,
Temperature -40.0 °C
 8692 psi

@Strain 0.540 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
64.99 MPa

@Strain 0.750 %,
Temperature 40.0 °C
 9426 psi

@Strain 0.750 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
70.7 MPa

@Strain 0.740 %,
Temperature 23.0 °C
 10300 psi

@Strain 0.740 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
76.73 MPa

@Strain 0.740 %,
Temperature 23.0 °C
 11130 psi

@Strain 0.740 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
81.39 MPa

@Strain 1.06 %,
Temperature 40.0 °C
 11800 psi

@Strain 1.06 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
85.54 MPa

@Strain 0.810 %,
Temperature -40.0 °C
 12410 psi

@Strain 0.810 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
87.91 MPa

@Strain 1.01 %,
Temperature 23.0 °C
 12750 psi

@Strain 1.01 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
92.6 MPa

@Strain 0.890 %,
Temperature -40.0 °C
 13400 psi

@Strain 0.890 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
100.96 MPa

@Strain 1.06 %,
Temperature 23.0 °C
 14643 psi

@Strain 1.06 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
111.33 MPa

@Strain 1.13 %,
Temperature -40.0 °C
 16147 psi

@Strain 1.13 %,
Temperature -40.0 °F
 50%RH; ISO 11403-1 -2
112.01 MPa

@Strain 2.21 %,
Temperature 40.0 °C
 16246 psi

@Strain 2.21 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
124.37 MPa

@Strain 1.29 %,
Temperature -40.0 °C
 18038 psi

@Strain 1.29 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2
125 MPa

@Strain 1.97 %,
Temperature 23.0 °C
 18100 psi

@Strain 1.97 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
Elongation at Break 2.0 %
2.0 %
50%RH; ISO 527-1/-2
2.2 %
2.2 %
DAM; ISO 527-1/-2
Tensile Modulus 10.5 GPa
1520 ksi
DAM; ISO 527-1/-2
10.5 GPa
1520 ksi
50%RH; ISO 527-1/-2
Flexural Strength 200 MPa
29000 psi
50%RH; ISO 178
230 MPa
33400 psi
DAM; ISO 178
Flexural Modulus 9.00 GPa
1310 ksi
DAM; ISO 178
10.0 GPa
1450 ksi
50%RH; ISO 178
Secant Modulus 1.98 GPa

@Strain 3.45 %,
Temperature 100 °C
 287 ksi

@Strain 3.45 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
2.69 GPa

@Strain 2.38 %,
Temperature 100 °C
 390 ksi

@Strain 2.38 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
2.85 GPa

@Strain 3.14 %,
Temperature 100 °C
 414 ksi

@Strain 3.14 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
3.562 GPa

@Strain 1.50 %,
Temperature 100 °C
 516.6 ksi

@Strain 1.50 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
3.80 GPa

@Strain 2.17 %,
Temperature 100 °C
 551 ksi

@Strain 2.17 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
4.80 GPa

@Strain 1.36 %,
Temperature 100 °C
 697 ksi

@Strain 1.36 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
4.84 GPa

@Strain 0.700 %,
Temperature 100 °C
 701 ksi

@Strain 0.700 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
5.18 GPa

@Strain 2.11 %,
Temperature 80.0 °C
 751 ksi

@Strain 2.11 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
6.07 GPa

@Strain 1.75 %,
Temperature 40.0 °C
 880 ksi

@Strain 1.75 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
6.14 GPa

@Strain 0.710 %,
Temperature 100 °C
 891 ksi

@Strain 0.710 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
6.42 GPa

@Strain 1.47 %,
Temperature 80.0 °C
 931 ksi

@Strain 1.47 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
6.43 GPa

@Strain 0.110 %,
Temperature 100 °C
 932 ksi

@Strain 0.110 %,
Temperature 212 °F
 50%RH; ISO 11403-1 -2
7.14 GPa

@Strain 1.27 %,
Temperature 40.0 °C
 1040 ksi

@Strain 1.27 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
7.16 GPa

@Strain 1.61 %,
Temperature 23.0 °C
 1040 ksi

@Strain 1.61 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
7.74 GPa

@Strain 0.930 %,
Temperature 80.0 °C
 1120 ksi

@Strain 0.930 %,
Temperature 176 °F
 DAM; ISO 11403-1 -2
7.79 GPa

@Strain 0.190 %,
Temperature 100 °C
 1130 ksi

@Strain 0.190 %,
Temperature 212 °F
 DAM; ISO 11403-1 -2
7.80 GPa

@Strain 1.83 %,
Temperature 23.0 °C
 1130 ksi

@Strain 1.83 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
8.07 GPa

@Strain 2.22 %,
Temperature -40.0 °C
 1170 ksi

@Strain 2.22 %,
Temperature -40.0 °F
 DAM; ISO 11403-1 -2