EPICHEM Epilac T ABS Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | EPICHEM srl |
| Trade Name | Epilac |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | EPICHEM Epilac T ABS Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 0.30 % <br>@Temperature 23.0 °C |
0.30 % <br>@Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Index of Compound | 6.0 - 11 g/10 min <br>@Load 12.0 kg,<br> Temperature 220 °C |
6.0 - 11 g/10 min <br>@Load 26.5 lb,<br> Temperature 428 °F |
ASTM D1238, ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638, ISO R527 |
| Elongation at Break | 20 % | 20 % | ASTM D638, ISO R527 |
| Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.500 - 0.600 J/cm <br>@Thickness 3.20 mm,<br> Temperature -30.0 °C |
0.937 - 1.12 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature -22.0 °F |
ASTM D256, ISO 180/4a |
| 0.700 - 1.10 J/cm <br>@Thickness 3.20 mm,<br> Temperature 0.000 °C |
1.31 - 2.06 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 32.0 °F |
ASTM D256, ISO 180/4a | |
| 1.20 - 1.50 J/cm <br>@Thickness 3.20 mm,<br> Temperature 23.0 °C |
2.25 - 2.81 ft-lb/in <br>@Thickness 0.126 in,<br> Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | >= 100 °C | >= 212 °F | BS 3456, IEC 335 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 105 - 110 °C <br>@Load 5.00 kg |
221 - 230 °F <br>@Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 115 - 118 °C <br>@Load 0.999 kg |
239 - 244 °F <br>@Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB <br>@Thickness 1.60 mm |
HB <br>@Thickness 0.0630 in |
|
| HB <br>@Thickness 3.20 mm |
HB <br>@Thickness 0.126 in |
||
| Glow Wire Test | 650 °C <br>@Thickness 3.20 mm |
1200 °F <br>@Thickness 0.126 in |
VDE 0471/P2-4, IEC 695 |
| 650 °C <br>@Thickness 2.00 mm |
1200 °F <br>@Thickness 0.0787 in |
VDE 0471/P2-4, IEC 695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.2 <br>@Frequency 1000 Hz |
3.2 <br>@Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.015 <br>@Frequency 1000 Hz |
0.015 <br>@Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- Eastman EASTALLOY Polymer DA105, Natural Alloy (discontinued **)
- Chevron Phillips 7120T LLDPE Cast/Blown Resin, Hexene Copolymer (discontinued **)
- Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure
- Chosun Refractories A65 Special High-Density Gunning Castable
- Akro-Plastic Akromid® A3 (2414) PA 6.6 Conditioned
- 3M Scotch-Weld™ TE030 Polyurethane Reactive Adhesive
- Overview of materials for Thermoplastic Olefinic Elastomer (TPO), Film Grade
- SABIC Innovative Plastics NORYL FR9310 PPE (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved