- Idemitsu Kosan Xarec® WA 214LG SPS, 40% Glass Filled
Idemitsu Kosan Xarec® WA 214LG SPS, 40% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber |
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Idemitsu Kosan Xarec® WA 214LG SPS, 40% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystalline Polymer, Glass Filled
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | |
| Filler Content | 40 % | 40 % | |
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | |
| Elongation at Break | 1.5 % | 1.5 % | |
| Tensile Modulus | 13.7 GPa | 1990 ksi | |
| Flexural Yield Strength | 220 MPa | 31900 psi | |
| Flexural Modulus | 13.2 GPa | 1910 ksi | |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | |
| Charpy Impact Unnotched | 4.20 J/cm² | 20.0 ft-lb/in² | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
8.33 µin/in-°F @Temperature -22.0 - 86.0 °F |
|
| CTE, linear, Transverse to Flow | 38.0 µm/m-°C | 21.1 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 270 °C | 518 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 3.1 | 3.1 | |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | ASTM D145 |
| Dissipation Factor | 0.0010 | 0.0010 | IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| 130 - 155 °C | 266 - 311 °F | For optimal surface finish |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comments | low outgassing @ elevated temperatures | |
| No mold release |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CM100LN Polypropylene, Impact Copolymer, Medium Impact, Nucleated, Antistat, Injection Molding
- PolyOne Geon™ Vinyl Flexible B85UB Polyvinyl Chloride, Flexible (PVC, Flexible)
- Solvay Specialty Polymers Cogegum® AFR/765 Polyolefin, Unspecified (Unverified Data**)
- Solvay TECHNYL® A 50H1 PA66, Conditioned
- SABIC Innovative Plastics LNP THERMOCOMP LX03447 PEEK
- Solvay GEROPON® CYA/75 Surfactant
- Topas Advanced Polymers TOPAS® 8007F-400 Cyclic Olefin Copolymer (COC)
- A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene
- ACC QM128 QSI Quantum Silicones 28 Durometer Condensation Cured Moldmaking Material
Copyright © lookpolymers.com All Rights Reserved