- LG Chemical LUMID HI2302A(W) PA6+GF30%, High Impact
LG Chemical LUMID HI2302A(W) PA6+GF30%, High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Impact Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI2302A(W) PA6+GF30%, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6+GF30%, High ImpactApplication: Automotive PartsCAS No. 25038-54-4, 9010-79-1 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0090 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 152 MPa @Thickness 3.20 mm |
22000 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 4.0 % @Thickness 3.20 mm |
4.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 235 MPa @Thickness 3.20 mm |
34100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 7.85 GPa @Thickness 3.20 mm |
1140 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 2.16 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
4.04 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C @Thickness 6.40 mm |
401 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 1.00 mm |
533 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 - 270 °C | 482 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 260 - 285 °C | 500 - 545 °F | Injection Molding |
| Front Barrel Temperature | 260 - 290 °C | 500 - 554 °F | Injection Molding |
| Nozzle Temperature | 260 - 290 °C | 500 - 554 °F | Injection Molding |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- RheTech Products P256-00 Polypropylene Copolymer, Natural
- LATI LASTANE 50 High Impact Polyurethane (PUR) (Unverified Data**)
- Silikony Polskie Polsilform Silicone Release Agent
- Teknor Apex Chemlon® 253 Nylon 6, Toughened
- TPI Porene® ABS-AN450 Flame Retardant ABS Resin
- Fainplast Compounds MPH 78/OP Medical Flexible PVC, Extrusion
- 3M Diamond Grade™ 983 Conspicuity Markings
- 3M Scotchcal™ 1000LF-10 Graphic Film
- Master Bond Supreme 3ANHT Epoxy Adhesives for Bonding Stainless Steel
Copyright © lookpolymers.com All Rights Reserved