Lanxess Durethan® AKV 35 LT H3.0 000000 Nylon 66, 35% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AKV 35 LT H3.0 000000 Nylon 66, 35% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, 35% glass fiberInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | 60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | 60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 123 MPa | 17800 psi | conditioned, 5 mm/min; ISO 527-1,-2 |
| 195 MPa | 28300 psi | 5 mm/min; ISO 527-1,-2 | |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1,-2 |
| 5.2 % | 5.2 % | conditioned, 5 mm/min; ISO 527-1,-2 | |
| Tensile Modulus | 8.10 GPa | 1170 ksi | conditioned, 1 mm/min; ISO 527-1,-2 |
| 11.5 GPa | 1670 ksi | 1 mm/min; ISO 527-1,-2 | |
| Flexural Strength | 214 MPa | 31000 psi | conditioned, 2 mm/min; ISO 178-A |
| 295 MPa | 42800 psi | 2 mm/min; ISO 178-A | |
| Flexural Modulus | 7.80 GPa | 1130 ksi | conditioned, 2 mm/min; ISO 178-A |
| 10.5 GPa | 1520 ksi | 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 179-1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Melting Point | 260 °C | 500 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 250 °C | >= 482 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1,-2 |
| Shrinkage | 0.100 % @Temperature 120 °C, Time 14400 sec |
0.100 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, 60x60x2; ISO 294-4 |
| 0.100 % @Temperature 120 °C, Time 14400 sec |
0.100 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, transverse, 60x60x2; ISO 294-4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
Users viewing this material also viewed the following:
- Nye Lubricants 793 (NG) Synthetic Oil
- Nylene® 609 Nylon 6, 50% RH, Film/Extrusion Grade
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N330 Filler
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Hardness 93A
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Sheet (0.015" thick)
- Zircar Ceramics SALI Moldable Alumina Insulation
- ChevronTexaco Delo® 2000 Marine Engine Oil, SAE 30
- Fainplast Compounds PH 61/K1-AM Flexible PVC, Transparent Extrusion
- Amco PRIMATOP PP HOMO 350NA Injection Molding Polypropylene
- 3M Scotch-Weld™ RT300B Rubber-Toughened Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved