Lanxess Pocan® B 4235 Z 000000 PBT, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® B 4235 Z 000000 PBT, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, 30% glass fibers, injection molding, flame retardant, impact modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 83 cm³/g | 83 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 |
| Melt Flow | 43 g/10 min @Load 5.00 kg, Temperature 260 °C |
43 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527-1/-2 |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527-1/-2 |
| Tensile Modulus | 9.80 GPa | 1420 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 130 °C | 266 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
IEC 60695-11-10 |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
IEC 60695-11-20 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Flame retarding agent | |
| Release agent | ||
| Features | Flame retardant | |
| High impact or high impact modified | ||
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GFHMPR,09-100,GF30; ISO 1043-PBT GF FR(17) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Omni Plastics OmniTech™ ABS GRC20 NA Glass Reinforced
- NOVA Chemicals Novapol® LM-0724-A LDPE Injection Molding Resin
- Plenco 50240 PET, Pellet, Injection Molded, Blue (discontinued **)
- Nilit FRIANYL C73 HS28 Nylon 6.6/6 for injection molding
- Heatbath/Park High Speed 75 High Speed Hardening Salt
- Teknor Apex APEX® 3610-70 Polyvinyl Chloride, Flexible
- Solvay JAGUAR® HP 120 Surfactant
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 60A, Non-Black Sulfur Cure
- CP-Polymer-Technik Wellamid® 6000 GV 30 HWCP 30% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- Asahi Kasei Thermofil D-30FG-1100 30% Glass Fiber Reinforced, ABS
Copyright © lookpolymers.com All Rights Reserved