Plastcom SLOVALEN PC 52 T 20 Polypropylene Copolymer, 20% Micronized Talc

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene with 20% Talc Filler
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVALEN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVALEN PC 52 T 20 Polypropylene Copolymer, 20% Micronized Talc.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesModified copolymer PP for injection moulding with the content of 20% micronized, floated, chemically modified talc. General application - packing material, garden flower-pots, toys, furniture industry, dowels, clamps, hinge, holders, office chairs, hangers, covers of car chassis, fenders, motors etc. Increased toughness. Delivered in natural and in the full RAL color scale. Heat stabilization enables the application in environment where it is subject to heat impact like the motor area.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
STN 64 0111
Linear Mold Shrinkage 0.0177 cm/cm
0.0177 in/in
STN 64 0808
Linear Mold Shrinkage, Transverse 0.0193 cm/cm
0.0193 in/in
STN 64 0808
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa
3630 psi
STN EN ISO 527-2
Elongation at Break 5.0 %
5.0 %
STN EN ISO 527-2
Tensile Modulus 2.50 GPa
363 ksi
STN EN ISO 527-2
Flexural Strength 70.0 MPa
10200 psi
STN EN ISO 178
Flexural Modulus 2.30 GPa
334 ksi
STN EN ISO 178
Charpy Impact Unnotched 1.50 J/cm²

@Temperature -20.0 °C
7.14 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
6.00 J/cm²

@Temperature 23.0 °C
28.6 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.200 J/cm²

@Temperature -20.0 °C
0.952 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 150 °C
302 °F
DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
STN EN ISO 75/A
Vicat Softening Point 85.0 °C
185 °F
B; STN EN ISO 306
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 40.0 - 50.0 °C
104 - 122 °F
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi