PolyOne Bergadur™ PB400 G30 UF UV Polybutylene Terephthalate (PBT)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergadur™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergadur™ PB400 G30 UF UV Polybutylene Terephthalate (PBT).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 - 100 MPa @Temperature 23.0 °C |
10900 - 14500 psi @Temperature 73.4 °F |
ISO 527-2/5 |
| Flexural Strength | 130 - 170 MPa | 18900 - 24700 psi | ISO 178 |
| Flexural Modulus | 0.00800 - 0.0100 GPa | 1.16 - 1.45 ksi | ISO 178 |
| Charpy Impact, Notched | 0.500 - 0.750 J/cm² @Temperature 23.0 °C |
2.38 - 3.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Unannealed; ISO 75-2/A |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 |
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 270 °C | 446 - 518 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | UV Stabilizer | |
| Features | Flame Retardant | |
| Halogen Free | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 30% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | PBT | |
| Generic Name | Polybutylene Terephthalate (PBT) | |
| Regional Availability | Asia Pacific |
Users viewing this material also viewed the following:
- Raschig Group SURAPLAST UPA 63 UP
- Lehmann & Voss LUVOCOM® 1800-8435 PET, with PTFE
- Kennametal Stellite Stellite® 3 PM with P/M Processing
- Teknor Apex Uniprene® UN-7100-55 Thermoplastic Vulcanizate
- Borealis Supercure™ LC8205R Polyethylene Insulation Compound, Crosslinkable
- A. Schulman POLYFORT™ FPP 3391 Chemically Coupled, Modified Polypropylene
- Covestro Bayblend® T65 AT PC/ABS Blend
- DSM Stanyl® TE250F9 Nylon 46-45% Glass Reinforced (European and Asian Grade) (Dry)
- Nye Lubricants 761 (NG) Synthetic Oil
Copyright © lookpolymers.com All Rights Reserved