SABIC Innovative Plastics LNP STAT-KON REL42 PA 66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON REL42 PA 66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-kon* REL42 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ASTM D792
1.32 g/cc
0.0477 lb/in³
ISO 1183
Moisture Absorption 0.600 %
0.600 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0036 cm/cm

@Time 86400 sec
0.0036 in/in

@Time 24.0 hour
ISO 294
0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.011 - 0.013 cm/cm

@Time 86400 sec
0.011 - 0.013 in/in

@Time 24.0 hour
ASTM D955
0.012 cm/cm

@Time 86400 sec
0.012 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 132 MPa
19100 psi
ASTM D638
133 MPa
19300 psi
ISO 527
Tensile Strength, Yield 132 MPa
19100 psi
ASTM D638
133 MPa
19300 psi
ISO 527
Elongation at Break 2.2 %
2.2 %
ISO 527
2.5 %
2.5 %
ASTM D638
Elongation at Yield 2.2 %
2.2 %
ISO 527
2.5 %
2.5 %
ASTM D638
Tensile Modulus 8.27 GPa
1200 ksi
50 mm/min; ASTM D638
8.69 GPa
1260 ksi
1 mm/min; ISO 527
Flexural Strength 186 MPa
27000 psi
ASTM D790
186 MPa
27000 psi
ISO 178
Flexural Modulus 7.40 GPa
1070 ksi
ISO 178
14.47 GPa
2099 ksi
ASTM D790
Izod Impact, Notched 0.420 J/cm
0.787 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.43 J/cm
8.30 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 29.0 kJ/m²
13.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 79.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
79.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 36.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
20.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
36.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
20.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 258 °C
496 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
260 °C

@Thickness 3.20 mm
500 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
247 °C

@Thickness 3.20 mm
477 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D257