SABIC Innovative Plastics LNP THERMOCOMP DF004P PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF004P PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DF004P is a Polycarbonate base resin containing Glass Fiber. Characteristics of this grade are Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 102 MPa | 14800 psi | 5 mm/min; ISO 527 |
| 106 MPa | 15400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 5 mm/min; ISO 527 |
| 43.0 MPa | 6240 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.33 GPa | 918 ksi | 1 mm/min; ISO 527 |
| 10.88 GPa | 1578 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 156 MPa | 22600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 202 MPa | 29300 psi | ISO 178 | |
| Flexural Modulus | 6.39 GPa | 927 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.54 GPa | 1819 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.43 J/cm | 13.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S EH 50A-3S7002 Thermoplastic Elastomer (TPE)
- Nanocyl AQUACYL™ AQ0101 Multi-Wall Carbon Nanotube Aqueous Dispersion
- Global EPP PA 6C MOLY Cast Polyamide 6 + MoS2
- LATI Latishield 66-10A PA66, Steel Fiber Reinforced
- Solvay Specialty Polymers Tecnoflon® T 636/L Fluoroelastomer
- SABIC Innovative Plastics LNP THERMOCOMP SF00A PA12 (Asia Pacific)
- Teknor Apex Monprene® MP-2740L3-UV Thermoplastic Elastomer
- A. Schulman SCHULAMID® 66 MV3H Unreinforced Nylon 6/6
- Eifeler Coatings Technology TiN PVD Coating
- SABIC Innovative Plastics Valox® VX4029 PBT (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved