Teijin Panlite® L-1250ZW Extrusion Grade Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Teijin
Trade Name Panlite®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Teijin Panlite® L-1250ZW Extrusion Grade Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Teijin Chemicals Ltd.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Water Absorption 0.20 %
0.20 %
in water, 23°C, 24h; ISO 62
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
<br>@Thickness 4.00 mm
 0.0050 - 0.0070 in/in
<br>@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
<br>@Thickness 4.00 mm
 0.0050 - 0.0070 in/in
<br>@Thickness 0.157 in
Melt Flow 8.4 g/10 min
<br>@Load 1.20 kg,<br> Temperature 300 °C
 8.4 g/10 min
<br>@Load 2.65 lb,<br> Temperature 572 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 62.0 MPa
8990 psi
50mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50mm/min; ISO 527
Tensile Modulus 2.40 GPa
348 ksi
1mm/min; ISO 527
Flexural Strength 93.0 MPa
13500 psi
2mm/min; ISO 178
Flexural Modulus 2.35 GPa
341 ksi
2mm/min; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 7.60 J/cm²
36.2 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C
<br>@Temperature 20.0 °C
 38.9 µin/in-°F
<br>@Temperature 68.0 °F
 ISO 11359
CTE, linear, Transverse to Flow 70.0 µm/m-°C
<br>@Temperature 20.0 °C
 38.9 µin/in-°F
<br>@Temperature 68.0 °F
 ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 142 °C
288 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
ISO 75
Vicat Softening Point 149 °C
300 °F
50°C/hr, 50N; ISO 306
UL RTI, Electrical 125 °C
<br>@Thickness 1.47 mm
 257 °F
<br>@Thickness 0.0579 in
 UL 746B
UL RTI, Mechanical with Impact 115 °C
<br>@Thickness 1.47 mm
 239 °F
<br>@Thickness 0.0579 in
 UL 746B
UL RTI, Mechanical without Impact 125 °C
<br>@Thickness 1.47 mm
 257 °F
<br>@Thickness 0.0579 in
 UL 746B
Flammability, UL94 HB
<br>@Thickness 1.50 mm
 HB
<br>@Thickness 0.0591 in
V-2
<br>@Thickness 0.400 mm
 V-2
<br>@Thickness 0.0157 in
Optical Properties Metric English Comments
Refractive Index 1.585
1.585
ASTM D542
Transmission, Visible 88 %
<br>@Thickness 3.00 mm
 88 %
<br>@Thickness 0.118 in
 ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.0
<br>@Frequency 1e+6 Hz
 3.0
<br>@Frequency 1e+6 Hz
 IEC 60250
3.1
<br>@Frequency 100 Hz
 3.1
<br>@Frequency 100 Hz
 IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243
Dissipation Factor 0.0010
<br>@Frequency 100 Hz
 0.0010
<br>@Frequency 100 Hz
 IEC 60250
0.0090
<br>@Frequency 1e+6 Hz
 0.0090
<br>@Frequency 1e+6 Hz
 IEC 60250
Comparative Tracking Index 250 V
250 V
IEC 60112