Teijin Panlite® LN-1010RM High Light Reflection, Flame Resistant Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Teijin |
| Trade Name | Panlite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Panlite® LN-1010RM High Light Reflection, Flame Resistant Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate-resin-base flame retardant and good light-reflection grade. It exhibits high light-reflection (over 96 %) at whole visible light range and also good light shut-out even at a thinner thickness portion.Applications:Electric and electronic components that need high light reflection and light shut-out.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % | 0.20 % | in water, 23°C, 24h; ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 50mm/min; ISO 527 |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50mm/min; ISO 527 |
| Elongation at Break | 110 % | 110 % | 50mm/min; ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 91.0 MPa | 13200 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ISO 75 |
| Vicat Softening Point | 139 °C | 282 °F | 50°C/hr, 50N; ISO 306 |
| UL RTI, Electrical | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C @Thickness 1.47 mm |
176 °F @Thickness 0.0579 in |
UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.380 mm |
V-0 @Thickness 0.0150 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 100 Hz |
3.4 @Frequency 100 Hz |
IEC 60250 |
| 3.4 @Frequency 1e+6 Hz |
3.4 @Frequency 1e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243 |
| Dissipation Factor | 0.0027 @Frequency 100 Hz |
0.0027 @Frequency 100 Hz |
IEC 60250 |
| 0.010 @Frequency 1e+6 Hz |
0.010 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
Users viewing this material also viewed the following:
- Overview of materials for Polytetrafluoroethylene (PTFE), Carbon Fiber Filled
- Lehmann & Voss LUVOCOM® 80/CF/10/BK Polyacetal-copolymer, with carbon fiber
- Materion Beryllium Copper Alloy 25 Plate & Rolled Bar; HT (TH04) Temper; over 25 to 51 mm Thickness (UNS C17200)
- Lehmann & Voss LUVOCOM® 50/TF/15/BK Polycarbonate, with PTFE
- Lucent Polymers POM-900P Acetal Homopolymer, Easy Flow, Injection Grade
- Shakespeare WP-500 diameter 0.5 mm Hydrolytically Stabilized Polyester Yarn
- SABIC Innovative Plastics LNP THERMOCOMP AX05466H ABS (Asia Pacific)
- A. Schulman PP 1930L-01 Polypropylene Copolymer Polypropylene
- Zircar Refractory Composites AL-HARD AL-HARD RIGIDIZER HARDENER
- BASF Ultramid® KR 4355 G5 BK 00564 25% Glass Filled PA6/6T (Dry)
Copyright © lookpolymers.com All Rights Reserved