BASF Ultramid® KR 4355 G10 BK 23215 50% Glass Filled PA6/6T (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® KR 4355 G10 BK 23215 50% Glass Filled PA6/6T (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 50% glass-fiber reinforced product for injection molding; high toughness and rigidity; low water absorption, high melting point (285°C); mechanical properties remain constant up to 60°C after moisture absorption; suitable e.g. for valve housings.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.62 g/cc
0.0585 lb/in³
ISO 1183
Water Absorption 3.5 - 4.5 %
3.5 - 4.5 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 0.40 - 0.80 %
0.40 - 0.80 %
23°C; 50% RH; ISO 62
Viscosity Measurement 135
135
ISO 307
Linear Mold Shrinkage 0.0029 cm/cm
0.0029 in/in
restricted
Linear Mold Shrinkage, Flow 0.0027 cm/cm
0.0027 in/in
TM=320°C, TW=100°C
0.0030 cm/cm
0.0030 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength, Yield 190 MPa
27600 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 2.5 %
2.5 %
ISO 527-1/-2
Modulus of Elasticity 16.0 GPa
2320 ksi
ISO 527-1/-2
Charpy Impact Unnotched 7.50 J/cm²

@Temperature -30.0 °C
35.7 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
8.00 J/cm²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Tensile Creep Modulus, 1000 hours 10500 MPa

@Strain <=0.500 %
1.52e+6 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
Specific Heat Capacity 1.00 J/g-°C
0.239 BTU/lb-°F
Thermal Conductivity 0.320 W/m-K
2.22 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 285 °C
545 °F
DIN 53765
Maximum Service Temperature, Air 145 °C
293 °F
for 50% loss of tensile strength after 20000hr
170 °C
338 °F
for 50% loss of tensile strength after 5000hr
260 °C
500 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
IEC 60093
Dielectric Constant 4.8

@Frequency 1.00 Hz
4.8

@Frequency 1.00 Hz
IEC 60250
Dielectric Strength 31.0 kV/mm
787 kV/in
IEC 60243-1
Dissipation Factor 0.030

@Frequency 1.00e+6 Hz
0.030

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 300 °C
572 °F
Feed Zone
Zone 2 310 °C
590 °F
Compression
Zone 3 320 °C
608 °F
Metering-zone
Zone 4 320 °C
608 °F
Nozzle
Melt Temperature 310 - 330 °C
590 - 626 °F
Injection-molding/Extrusion
320 °C
608 °F
Optimal
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Injection-molding
100 °C
212 °F
Optimal
Drying Temperature 110 °C
230 °F
Dry Time 8 hour
8 hour
Moisture Content <= 0.030 %
<= 0.030 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Color BK 23215
Commercial Status Europe
Peripheral screw speed <0.3 m/s