BASF Ultrason S 3010 PSU

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer BASF
Trade Name Ultrason S
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultrason S 3010 PSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultrason S 3010 is an unreinforced, higher viscosity injection molding and extrusion PSU grade, tougher and with improved chemical resistance. It conforms to FDA requirements of 21 CFR 177.1655.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Moisture Absorption at Equilibrium 0.30 %
0.30 %
23°C/50% R.H.; ISO 62
Viscosity Test 72 cm³/g
72 cm³/g
Viscosity number
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
ISO 294
Linear Mold Shrinkage, Transverse 0.0074 cm/cm
0.0074 in/in
ISO 294
Melt Flow 40 g/10 min

@Load 10.0 kg,
Temperature 360 °C
40 g/10 min

@Load 22.0 lb,
Temperature 680 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 135 MPa
19600 psi
ISO 2039-1
Tensile Strength at Break 75.0 MPa
10900 psi
5mm/min; ISO 527-2
Tensile Stress 20.0 MPa

@Strain 1.00 %,
Temperature 160 °C
2900 psi

@Strain 1.00 %,
Temperature 320 °F
ISO 527
27.0 MPa

@Strain 1.00 %,
Temperature 23.0 °C
3920 psi

@Strain 1.00 %,
Temperature 73.4 °F
ISO 527
35.0 MPa

@Strain 2.00 %,
Temperature 160 °C
5080 psi

@Strain 2.00 %,
Temperature 320 °F
ISO 527
47.0 MPa

@Strain 2.00 %,
Temperature 23.0 °C
6820 psi

@Strain 2.00 %,
Temperature 73.4 °F
ISO 527
70.0 MPa

@Strain 4.00 %,
Temperature 23.0 °C
10200 psi

@Strain 4.00 %,
Temperature 73.4 °F
ISO 527
Tensile Strength, Yield 75.0 MPa
10900 psi
50mm/min; ISO 527-2
40.0 MPa

@Temperature 140 °C
5800 psi

@Temperature 284 °F
58.0 MPa

@Temperature 100 °C
8410 psi

@Temperature 212 °F
68.0 MPa

@Temperature 60.0 °C
9860 psi

@Temperature 140 °F
75.0 MPa

@Temperature 20.0 °C
10900 psi

@Temperature 68.0 °F
Elongation at Break 5.7 %
5.7 %
5mm/min; ISO 527-2
Elongation at Yield 5.7 %
5.7 %
50mm/min; ISO 527-2
0.50 %

@Time 3600 sec,
Pressure 10.0 MPa
0.50 %

@Time 1.00 hour,
Pressure 1450 psi
ISO 899
0.55 %

@Pressure 10.0 MPa,
Time 360000 sec
0.55 %

@Pressure 1450 psi,
Time 100 hour
ISO 899
0.56 %

@Pressure 10.0 MPa,
Time 3.60e+7 sec
0.56 %

@Pressure 1450 psi,
Time 10000 hour
ISO 899
0.80 %

@Time 3600 sec,
Pressure 20.0 MPa
0.80 %

@Time 1.00 hour,
Pressure 2900 psi
ISO 899
0.90 %

@Pressure 20.0 MPa,
Time 360000 sec
0.90 %

@Pressure 2900 psi,
Time 100 hour
ISO 899
1.3 %

@Time 3600 sec,
Pressure 30.0 MPa
1.3 %

@Time 1.00 hour,
Pressure 4350 psi
ISO 899
1.4 %

@Pressure 30.0 MPa,
Time 360000 sec
1.4 %

@Pressure 4350 psi,
Time 100 hour
ISO 899
1.5 %

@Pressure 30.0 MPa,
Time 3.60e+7 sec
1.5 %

@Pressure 4350 psi,
Time 10000 hour
ISO 899
1.9 %

@Time 3600 sec,
Pressure 40.0 MPa
1.9 %

@Time 1.00 hour,
Pressure 5800 psi
ISO 899
2.0 %

@Pressure 20.0 MPa,
Time 3.60e+7 sec
2.0 %

@Pressure 2900 psi,
Time 10000 hour
ISO 899
2.0 %

@Pressure 40.0 MPa,
Time 360000 sec
2.0 %

@Pressure 5800 psi,
Time 100 hour
ISO 899
2.0 %

@Time 3600 sec,
Pressure 42.0 MPa
2.0 %

@Time 1.00 hour,
Pressure 6090 psi
ISO 899
2.2 %

@Pressure 42.0 MPa,
Time 360000 sec
2.2 %

@Pressure 6090 psi,
Time 100 hour
ISO 899
2.4 %

@Pressure 40.0 MPa,
Time 3.60e+7 sec
2.4 %

@Pressure 5800 psi,
Time 10000 hour
ISO 899
2.5 %

@Pressure 42.0 MPa,
Time 3.60e+7 sec
2.5 %

@Pressure 6090 psi,
Time 10000 hour
ISO 899
Creep Strength 17.0 MPa

@Time 3.60e+7 sec
2470 psi

@Time 10000 hour
in water at 95°C
20.0 MPa

@Time 3.60e+6 sec
2900 psi

@Time 1000 hour
in water at 95°C
25.0 MPa

@Time 360000 sec
3630 psi

@Time 100 hour
in water at 95°C
32.0 MPa

@Time 36000 sec
4640 psi

@Time 10.0 hour
in water at 95°C
Modulus of Elasticity 2.00 GPa

@Temperature 140 °C
290 ksi

@Temperature 284 °F
ISO 527
2.30 GPa

@Temperature 100 °C
334 ksi

@Temperature 212 °F
ISO 527
2.49 GPa

@Temperature 60.0 °C
361 ksi

@Temperature 140 °F
ISO 527
2.51 GPa

@Temperature 20.0 °C
364 ksi

@Temperature 68.0 °F
ISO 527
Tensile Modulus 2.60 GPa
377 ksi
ISO 527-2
Fatigue Strength 25.0 MPa

@# of Cycles 1.00e+7
3630 psi

@# of Cycles 1.00e+7
30.0 MPa

@# of Cycles 1.00e+6
4350 psi

@# of Cycles 1.00e+6
40.0 MPa

@# of Cycles 100000
5800 psi

@# of Cycles 100000
50.0 MPa

@# of Cycles 10000
7250 psi

@# of Cycles 10000
Shear Modulus 0.0250 GPa

@Temperature 200 °C
3.63 ksi

@Temperature 392 °F
ISO 6721
0.800 GPa

@Temperature 175 °C
116 ksi

@Temperature 347 °F
ISO 6721
0.900 GPa

@Temperature 100 °C
131 ksi

@Temperature 212 °F
ISO 6721
0.950 GPa

@Temperature 50.0 °C
138 ksi

@Temperature 122 °F
ISO 6721
Izod Impact, Notched (ISO) 5.50 kJ/m²
2.62 ft-lb/in²
ISO 180/A
5.00 kJ/m²

@Temperature 120 °C
2.38 ft-lb/in²

@Temperature 248 °F
ISO 179/1eA
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 180/A
10.0 kJ/m²

@Temperature 50.0 °C
4.76 ft-lb/in²

@Temperature 122 °F
ISO 179/1eA
13.0 kJ/m²

@Temperature -25.0 °C
6.19 ft-lb/in²

@Temperature -13.0 °F
ISO 179/1eA
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 2500 MPa
363000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 53.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
29.4 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
60.0 µm/m-°C

@Temperature 140 - 180 °C
33.3 µin/in-°F

@Temperature 284 - 356 °F
ISO 11359-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
IEC 60093
Dielectric Constant 3.1

@Frequency 100 Hz
3.1

@Frequency 100 Hz
IEC 60250
3.1

@Frequency 1.00e+6 Hz
3.1

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 37.0 kV/mm
940 kV/in
IEC 60243-1
Dissipation Factor 0.00080

@Frequency 100 Hz
0.00080

@Frequency 100 Hz
IEC 60250
0.0064

@Frequency 1.00e+6 Hz
0.0064

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 125 V
125 V
Test Liquid A & B; IEC 60112