Dow TUFLIN™ HS-7065 NT 7 Linear Low Density Polyethylene Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Dow Chemical
Trade Name TUFLIN™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow TUFLIN™ HS-7065 NT 7 Linear Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hexene Linear Low Density Resin Good Processability at Narrow Die Gaps Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a TUFLIN™ HS-7065 NT 7 is a fractional melt, ethylene-hexene copolymer, designed for good toughness and stiffness. This product is recommended for thin and thick gauge applications such as trash bags and heavy-duty shipping sacks that require strength and output.Information provided by Dow
Physical Properties Metric English Comments
Density 0.9289 g/cc
0.03356 lb/in³
ASTM D792
Thickness 50.8 microns
2.00 mil
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 4000 ppm
4000 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 16.22 MPa
2352 psi
ASTM D882
Film Tensile Strength at Yield, TD 16.14 MPa
2341 psi
ASTM D882
Film Elongation at Break, MD 860 %
860 %
ASTM D882
Film Elongation at Break, TD 817 %
817 %
ASTM D882
Secant Modulus, MD 0.2985 GPa
43.29 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.2629 GPa
38.13 ksi
2% Secant; ASTM D882
Impact 18
18
[lb<sub>f</sub>]; Puncture Resistance Force; Dow Method
118
118
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
4007
4007
[ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882
4785
4785
[ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882
Puncture Energy 4.63 J
3.42 ft-lb
Dow Method
Elmendorf Tear Strength MD 928 g
928 g
Method B; ASTM D1922
Elmendorf Tear Strength TD 1120 g
1120 g
Method B; ASTM D1922
Elmendorf Tear Strength, MD 18.3 g/micron
464 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 22.0 g/micron
560 g/mil
ASTM D1922
Dart Drop Test <= 100 g
<= 0.221 lb
Method B; ASTM D1709
304 g
0.670 lb
Method A; ASTM D1709
Film Tensile Strength at Break, MD 53.33 MPa
7735 psi
ASTM D882
Film Tensile Strength at Break, TD 45.04 MPa
6533 psi
ASTM D882
Heat Seal Strength, Ultimate 23.1 N
5.19 lb (f)
at 160°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Heat Seal Strength Initiation Temperature 120 °C
248 °F
1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Thermal Properties Metric English Comments
Melting Point 126 °C
259 °F
Dow Method (DSC)
Vicat Softening Point 116 °C
241 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 15 %
15 %
ASTM D1003
Gloss 73 %
73 %
45°; ASTM D2457
78 %
78 %
20°; ASTM D2457