Huntsman PE1055 Film Extrusion Polyethylene  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE1055 Film Extrusion Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Homopolymer, and FDA compliant.Features: Yields film with excellent optical and draw down characteristicsApplications: Film extrusion: soft goods and other high clarity packaging.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under condition of use B through H described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 3.0 g/10 min
3.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 54
54
ASTM D2240
Tensile Strength, Ultimate 10.0 MPa
1450 psi
ASTM D638
Tensile Strength, Yield 11.0 MPa
1600 psi
ASTM D638
Film Elongation at Break, MD 350 %
350 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Elongation at Break 375 %
375 %
ASTM D638
Modulus of Elasticity 0.255 GPa
37.0 ksi
Secant; ASTM D638
Secant Modulus, MD 0.207 GPa
30.0 ksi
ASTM D882
Secant Modulus, TD 0.242 GPa
35.1 ksi
ASTM D882
Dart Drop 1.77 g/micron
45.0 g/mil
ASTM D1709
Dart Drop Test 45.0 g
0.0992 lb
ASTM D1709
Film Tensile Strength at Break, MD 19.0 MPa
2760 psi
ASTM D882
Film Tensile Strength at Break, TD 17.0 MPa
2470 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 96.0 °C
205 °F
ASTM D1525
Optical Properties Metric English Comments
Gloss 63 %
63 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 171 - 182 °C
340 - 360 °F