Industeel CLC 18.10Ti Titanium-Stabilized 18Cr-10Ni Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel , T S30000 Series Stainless Steel
Manufacturer Groupe Arcelor
Trade Name CLC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industeel CLC 18.10Ti Titanium-Stabilized 18Cr-10Ni Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CLC 18-10Ti is a 18Cr-9Ni austenitic stainless steel stabilized with some Titanium additions. This is a basic grades in the stainless steel range. Titanium bearing (carbide forming element) avoids intergranular corrosion, even on welded pieces without ulterior water quenching. Alloys CLC 18-10Ti exhibit austenitic microstructures free of deleterious carbide precipitations but with CNTi precipitations at the grain boundaries. The grade contains some residual ferrite (~ 4%) after solution annealing (1000-1100°C – 1832-2012°F) and water quenching. The main properties are :Basic corrosion resistanceResistance against intergranular corrosionHeat resistant alloy (medium temperature)High ductilityInformation provided by manufacturer.
Physical Properties Metric English Comments
Density 7.95 g/cc
0.287 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 600 MPa
87000 psi
Typical
500 - 700 MPa
72500 - 102000 psi
Minimum Guaranteed
Tensile Strength, Yield >= 200 MPa

@Strain 0.200 %
>= 29000 psi

@Strain 0.200 %
>= 240 MPa

@Strain 1.00 %
>= 34800 psi

@Strain 1.00 %
280 MPa

@Strain 0.200 %
40600 psi

@Strain 0.200 %
Typical
310 MPa

@Strain 1.00 %
45000 psi

@Strain 1.00 %
Typical
Elongation at Break 45 %
45 %
Creep Strength 300 MPa

@Temperature 600 °C,
Time 3.60e+6 sec
43500 psi

@Temperature 1110 °F,
Time 1000 hour
Modulus of Elasticity 200 GPa

@Temperature 20.0 - 100 °C
29000 ksi

@Temperature 68.0 - 212 °F
Poissons Ratio 0.299
0.299
Calculated
Shear Modulus 77.0 GPa

@Temperature 20.0 - 100 °C
11200 ksi

@Temperature 68.0 - 212 °F
Charpy Impact >= 150 J
>= 111 ft-lb
225 J
166 ft-lb
Typical
>= 62.0 J

@Temperature -269 °C
>= 45.7 ft-lb

@Temperature -452 °F
138 J

@Temperature -269 °C
102 ft-lb

@Temperature -452 °F
Typical
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C

@Temperature 20.0 - 100 °C
8.89 µin/in-°F

@Temperature 68.0 - 212 °F
16.5 µm/m-°C

@Temperature 20.0 - 200 °C
9.17 µin/in-°F

@Temperature 68.0 - 392 °F
17.0 µm/m-°C

@Temperature 20.0 - 300 °C
9.44 µin/in-°F

@Temperature 68.0 - 572 °F
18.0 µm/m-°C

@Temperature 20.0 - 500 °C
10.0 µin/in-°F

@Temperature 68.0 - 932 °F
Specific Heat Capacity 0.500 J/g-°C

@Temperature 20.0 - 100 °C
0.120 BTU/lb-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 15.0 W/m-K

@Temperature 20.0 - 100 °C
104 BTU-in/hr-ft²-°F

@Temperature 68.0 - 212 °F
Component Elements Properties Metric English Comments
Carbon, C 0.050 %
0.050 %
Chromium, Cr 17.5 %
17.5 %
Iron, Fe 72.55 - 73 %
72.55 - 73 %
As remainder
Nickel, Ni 9.2 %
9.2 %
Titanium, Ti 0.25 - 0.70 %
0.25 - 0.70 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000730 ohm-cm

@Temperature 20.0 - 100 °C
0.0000730 ohm-cm

@Temperature 68.0 - 212 °F