Industrial Laminates/Norplex NP634 Laminate

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP634 Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Warm punching, composite grade with woven glass covers for improved flexural, tensile and impact strength. Electrical properties comparable to NP611.Thickness Tested: 0.062", 0.125" and 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.35 - 1.45 g/cc

@Thickness 1.57 mm
 1.35 - 1.45 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 0.72 %

@Thickness 1.57 mm
 0.72 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 85 - 105

@Thickness 1.57 mm
 85 - 105

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 139 MPa

@Thickness 1.57 mm
 20100 psi

@Thickness 0.0620 in
 CW; ASTM D638
165 MPa

@Thickness 1.57 mm
 23900 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 10.3 GPa

@Thickness 1.57 mm
 1500 ksi

@Thickness 0.0620 in
 CW; ASTM D229
12.4 GPa

@Thickness 1.57 mm
 1800 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 308 MPa

@Thickness 1.57 mm
 44600 psi

@Thickness 0.0620 in
 CW; ASTM D790
356 MPa

@Thickness 1.57 mm
 51600 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 286 MPa

@Thickness 12.7 mm
 41500 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 96.5 MPa

@Thickness 15.7 mm
 14000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 1.17 J/cm

@Thickness 12.7 mm
 2.20 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
1.76 J/cm

@Thickness 12.7 mm
 3.30 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 15.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 8.33 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 13.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 7.22 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 125 °C
257 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 5.2

@Thickness 1.57 mm
 5.2

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 21.7 kV/mm

@Thickness 1.57 mm
 550 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
23.6 kV/mm

@Thickness 1.57 mm
 600 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 7000 V

@Thickness 1.57 mm
 7000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
53000 V

@Thickness 1.57 mm
 53000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.037

@Thickness 1.57 mm
 0.037

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 120 sec

@Thickness 3.17 mm
 120 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 200 V

@Thickness 3.17 mm
 200 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1500 lb
0.5", ASTM D229
Color Natural, Black