LATI Kelon® A FR H2 CETG/300-V0 PA 66, Glass/Mineral Reinforced, Flame Retardant, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant , Nylon 66, Glass/Mineral Filled
Manufacturer LATI
Trade Name Kelon® A
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Kelon® A FR H2 CETG/300-V0 PA 66, Glass/Mineral Reinforced, Flame Retardant, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers / Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. Low thermal expansion coefficient. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.61 g/cc
0.0582 lb/in³
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0075 cm/cm
0.0055 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa

@Temperature 150 °C
 4350 psi

@Temperature 302 °F
35.0 MPa

@Temperature 120 °C
 5080 psi

@Temperature 248 °F
45.0 MPa

@Temperature 90.0 °C
 6530 psi

@Temperature 194 °F
65.0 MPa

@Temperature 60.0 °C
 9430 psi

@Temperature 140 °F
80.0 MPa

@Temperature 23.0 °C
 11600 psi

@Temperature 73.4 °F
Elongation at Break 1.6 %

@Temperature 23.0 °C
 1.6 %

@Temperature 73.4 °F
2.7 %

@Temperature 60.0 °C
 2.7 %

@Temperature 140 °F
6.5 %

@Temperature 90.0 °C
 6.5 %

@Temperature 194 °F
12 %

@Temperature 120 °C
 12 %

@Temperature 248 °F
20 %

@Temperature 150 °C
 20 %

@Temperature 302 °F
Elongation at Yield 5.0 %

@Temperature 90.0 °C
 5.0 %

@Temperature 194 °F
7.0 %

@Temperature 120 °C
 7.0 %

@Temperature 248 °F
10 %

@Temperature 150 °C
 10 %

@Temperature 302 °F
Tensile Modulus 2.80 GPa

@Temperature 150 °C
 406 ksi

@Temperature 302 °F
3.30 GPa

@Temperature 120 °C
 479 ksi

@Temperature 248 °F
4.80 GPa

@Temperature 90.0 °C
 696 ksi

@Temperature 194 °F
8.00 GPa

@Temperature 60.0 °C
 1160 ksi

@Temperature 140 °F
10.2 GPa

@Temperature 23.0 °C
 1480 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
2.00 J/cm²

@Temperature -20.0 °C
 9.52 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.200 J/cm²

@Temperature 23.0 °C
 0.952 ft-lb/in²

@Temperature 73.4 °F
0.200 J/cm²

@Temperature -20.0 °C
 0.952 ft-lb/in²

@Temperature -4.00 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 115 °C
239 °F
Deflection Temperature at 0.46 MPa (66 psi) 240 °C
464 °F
Deflection Temperature at 1.8 MPa (264 psi) 220 °C
428 °F
Vicat Softening Point 235 °C

@Load 5.00 kg
 455 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 36 %
36 %
Glow Wire Test 775 °C

@Thickness 2.00 mm
 1430 °F

@Thickness 0.0787 in
 GWIT
850 °C

@Thickness 1.00 mm
 1560 °F

@Thickness 0.0394 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 400 V
400 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa