Lanxess Durethan® B 30 S F30 000000 Nylon 6, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® B 30 S F30 000000 Nylon 6, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, non-reinforced, injection molding, flame retardantInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.35 g/cc
1.35 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.00040 cm/cm
0.00040 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.011 cm/cm
0.011 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.00040 cm/cm
0.00040 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.011 cm/cm
0.011 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 70.0 MPa
10200 psi
d.a.m.; ISO 527-1, -2; 50 mm/min
Elongation at Break 9.0 %
9.0 %
d.a.m.; ISO 527-1, -2; 50 mm/min
Elongation at Yield 3.7 %
3.7 %
d.a.m.; ISO 527-1, -2; 50 mm/min
Tensile Modulus 3.60 GPa
522 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 110 MPa

@Strain 5.50 %
 16000 psi

@Strain 5.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 100 MPa

@Strain 3.50 %
 14500 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 3.20 GPa
464 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1A
Izod Impact, Unnotched (ISO) 100 kJ/m²

@Temperature -30.0 °C
 47.6 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
120 kJ/m²

@Temperature 23.0 °C
 57.1 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
Charpy Impact Unnotched 13.0 J/cm²

@Temperature -30.0 °C
 61.9 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
15.0 J/cm²

@Temperature 23.0 °C
 71.4 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
ISO 75-1, -2
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
5VA

@Thickness 2.00 mm
 5VA

@Thickness 0.0787 in
5VA

@Thickness 3.00 mm
 5VA

@Thickness 0.118 in
Glow Wire Test 800 °C

@Diameter 3.00 mm
 1470 °F

@Diameter 0.118 in
 GWIT; IEC 60695-2-13
825 °C

@Diameter 0.750 mm
 1520 °F

@Diameter 0.0295 in
 GWIT; IEC 60695-2-13
825 °C

@Diameter 1.50 mm
 1520 °F

@Diameter 0.0591 in
 GWIT; IEC 60695-2-13
960 °C

@Diameter 0.800 mm
 1760 °F

@Diameter 0.0315 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 1.50 mm
 1760 °F

@Diameter 0.0591 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 3.00 mm
 1760 °F

@Diameter 0.118 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 300 V
300 V
d.a.m.; Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
for test specimens; ISO 294
260 °C
500 °F
admissible residence time at Tmax >= 10 min
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, GFHR, 14-040; ISO 1043-PA GF FR (17)