Overview of materials for Polycarbonate, Foam Grade, Glass Filled

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Foam Grade, Glass Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polycarbonate, Foam Grade, Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Foam Grade, Glass Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.21 - 1.43 g/cc
0.0437 - 0.0517 lb/in³
Average value: 1.30 g/cc Grade Count:10
Linear Mold Shrinkage 0.00100 - 0.00700 cm/cm
0.00100 - 0.00700 in/in
Average value: 0.00443 cm/cm Grade Count:7
Melt Flow 3.00 - 25.0 g/10 min
3.00 - 25.0 g/10 min
Average value: 11.6 g/10 min Grade Count:9
Mechanical Properties Metric English Comments
Hardness, Rockwell M 70.0
70.0
Average value: 70.0 Grade Count:3
Tensile Strength, Ultimate 45.0 - 124 MPa
6530 - 18000 psi
Average value: 73.3 MPa Grade Count:10
Tensile Strength, Yield 55.2 - 124 MPa
8000 - 18000 psi
Average value: 78.3 MPa Grade Count:7
Flexural Yield Strength 94.8 - 152 MPa
13800 - 22000 psi
Average value: 115 MPa Grade Count:7
Flexural Modulus 3.10 - 6.89 GPa
450 - 1000 ksi
Average value: 4.61 GPa Grade Count:7
Izod Impact, Notched 0.801 - 6.41 J/cm
1.50 - 12.0 ft-lb/in
Average value: 3.27 J/cm Grade Count:8
Izod Impact, Notched (ISO) 8.00 - 8.00 kJ/m²

@Temperature -30.0 - -30.0 °C
3.81 - 3.81 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 8.00 kJ/m² Grade Count:1
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 138 - 152 °C
280 - 305 °F
Average value: 142 °C Grade Count:7
Deflection Temperature at 1.8 MPa (264 psi) 131 - 146 °C
268 - 295 °F
Average value: 137 °C Grade Count:10
Vicat Softening Point 145 - 154 °C
293 - 310 °F
Average value: 152 °C Grade Count:4
Flammability, UL94 V-2 - V-0
V-2 - V-0
Grade Count:8
Processing Properties Metric English Comments
Processing Temperature 266 - 288 °C
510 - 550 °F
Average value: 277 °C Grade Count:3
Melt Temperature 254 - 338 °C
490 - 640 °F
Average value: 296 °C Grade Count:7
Mold Temperature 71.1 - 116 °C
160 - 240 °F
Average value: 92.5 °C Grade Count:7
Drying Temperature 118 - 127 °C
245 - 260 °F
Average value: 123 °C Grade Count:9