Raschig Group EPOXIDUR® 3580 EP Epoxy

Category Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler , Filled/Reinforced Thermoset
Manufacturer Raschig Group
Trade Name EPOXIDUR®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group EPOXIDUR® 3580 EP Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass-fiber reinforced and mineral filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties even with thin wall thicknesses and high temperatures. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection and compression molding Primary application: Electrical partsInformation provided by the Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.90 - 2.00 g/cc
1.90 - 2.00 g/cc
ISO 1183
Apparent Bulk Density 0.600 - 0.900 g/cc
0.0217 - 0.0325 lb/in³
ISO 60
Water Absorption <= 0.10 %

@Temperature 23.0 °C,
Time 86400 sec
<= 0.10 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
(longitudinal) Injection and Compression; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength, Yield 30.0 - 50.0 MPa
4350 - 7250 psi
Injection and Compression; ISO 527
Modulus of Elasticity 14.0 - 16.0 GPa
2030 - 2320 ksi
Injection and Compression; ISO 527
Flexural Strength 70.0 - 100 MPa
10200 - 14500 psi
Injection and Compression; ISO 178
Flexural Modulus 17.0 - 20.0 GPa
2470 - 2900 ksi
Injection and Compression; ISO 178
Compressive Strength 150 - 180 MPa
21800 - 26100 psi
ISO 604
Charpy Impact Unnotched 0.400 - 0.600 J/cm²

@Temperature 23.0 °C
1.90 - 2.86 ft-lb/in²

@Temperature 73.4 °F
Injection and Compression; ISO 179/ 1eU
Charpy Impact, Notched 0.200 - 0.400 J/cm²

@Temperature 23.0 °C
0.952 - 1.90 ft-lb/in²

@Temperature 73.4 °F
Injection and Compression; ISO 179/ 1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 - 20.0 µm/m-°C

@Temperature 50.0 - 150 °C
8.33 - 11.1 µin/in-°F

@Temperature 122 - 302 °F
ISO 11359-2
Thermal Conductivity 0.400 - 0.600 W/m-K
2.78 - 4.16 BTU-in/hr-ft²-°F
ASTM E1461
Maximum Service Temperature, Air 180 °C

@Time 7.20e+7 sec
356 °F

@Time 20000 hour
IEC 60216/T1
240 °C

@Time <=180000 sec
464 °F

@Time <=50.0 hour
IEC 60216/T1
Deflection Temperature at 0.46 MPa (66 psi) >= 200 °C
>= 392 °F
Injection; ISO 75-B
Deflection Temperature at 1.8 MPa (264 psi) >= 200 °C
>= 392 °F
Injection and Compression; ISO 75-A
Deflection Temperature at 8.0 MPa 180 - 200 °C
356 - 392 °F
Injection and Compression; ISO 75-C
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
V-0

@Thickness 6.00 mm
V-0

@Thickness 0.236 in
Shrinkage <= 0.050 %

@Temperature 110 °C,
Time 605000 sec
<= 0.050 %

@Temperature 230 °F,
Time 168 hour
ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 - 1.00e+16 ohm-cm
1.00e+15 - 1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 - 1.00e+15 ohm
1.00e+14 - 1.00e+15 ohm
IEC 60093
Dielectric Constant 4.0 - 6.0

@Frequency 1.00e+6 Hz
4.0 - 6.0

@Frequency 1.00e+6 Hz
IEC 60250
5.0 - 7.0

@Frequency 100 Hz
5.0 - 7.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 30.0 - 40.0 kV/mm
762 - 1020 kV/in
IEC 60243-1
Dissipation Factor 0.010 - 0.030

@Frequency 1.00e+6 Hz
0.010 - 0.030

@Frequency 1.00e+6 Hz
IEC 60250
0.030 - 0.050

@Frequency 100 Hz
0.030 - 0.050

@Frequency 100 Hz
IEC 60250
Comparative Tracking Index >= 250 V
>= 250 V
CTI; IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature <=20.0 °C
6.00 Month

@Temperature <=68.0 °F
Descriptive Properties Value Comments
Arc Resistance 4 Stufe
ASTM D495
Glow wire flammability test 900/1
IEC 60695 2-12
Glow wire ignitability test 900/1
IEC 60695 2-13
Water Absorption <10 mg
24h/23°C; ISO 62