Material Notes:
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ASTM D 792
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.65 %
0.65 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.2 %

@Temperature 23.0 °C
1.2 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
on tensile bar; SABIC Method
0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 6.60 kg,
Temperature 337 °C
16 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
21 g/10 min

@Load 5.00 kg,
Temperature 360 °C
21 g/10 min

@Load 11.0 lb,
Temperature 680 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
5 mm/min; ISO 527
85.0 MPa
12300 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 110 MPa
16000 psi
Type I, 5 mm/min; ASTM D 638
110 MPa
16000 psi
5 mm/min; ISO 527
Elongation at Break 60 %
60 %
5 mm/min; ISO 527
70 %
70 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 6.0 %
6.0 %
5 mm/min; ISO 527
7.0 %
7.0 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 3.50 GPa
508 ksi
1 mm/min; ISO 527
3.72 GPa
540 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 140 MPa
20300 psi
2 mm/min; ISO 178
165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 3.30 GPa
479 ksi
2 mm/min; ISO 178
3.72 GPa
540 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.560 J/cm

@Temperature 23.0 °C
1.05 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
19.2 J/cm

@Thickness 3.20 mm
36.0 ft-lb/in

@Thickness 0.126 in
reverse notched; ASTM D 256
Izod Impact, Unnotched 21.0 J/cm

@Temperature 23.0 °C
39.3 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
1.90 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
80*10*4; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Gardner Impact 23.0 J

@Temperature 23.0 °C
17.0 ft-lb

@Temperature 73.4 °F
ASTM D 3029
Impact Test 28.0 J

@Temperature 23.0 °C
20.7 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
55.0 µm/m-°C

@Temperature -40.0 - 150 °C
30.6 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
55.0 µm/m-°C

@Temperature -40.0 - 150 °C
30.6 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
Thermal Conductivity 0.260 W/m-K
1.80 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
207 °C

@Thickness 3.20 mm
405 °F

@Thickness 0.126 in
unannealed; ASTM D 648
210 °C

@Thickness 6.40 mm
410 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
197 °C

@Thickness 3.20 mm
387 °F

@Thickness 0.126 in
unannealed; ASTM D 648
199 °C

@Thickness 6.40 mm
390 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Vicat Softening Point 200 °C
392 °F
Rate B/50; ISO 306
205 °C
401 °F
Rate B/120; ISO 306
210 °C
410 °F
Rate A/50; ISO 306
219 °C
426 °F
Rate B/50; ASTM D 1525
Glass Transition Temp, Tg 217 °C
423 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.5

@Frequency 50.0 - 60.0 Hz
3.5

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 17.2 kV/mm

@Thickness 3.20 mm
437 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0016

@Frequency 50.0 - 60.0 Hz
0.0016

@Frequency 50.0 - 60.0 Hz
IEC 60250
Comparative Tracking Index >= 125 V
>= 125 V
IEC 60112
175 V
175 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2