Unitika PT-3020
| Category | Polymer , Thermoplastic , Polyarylate |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika PT-3020.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: Dimensional accuracy (planarity) Heat resistance Creep resistance and elasticity RigidityInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| Water Absorption | 0.12 % @Thickness 3.17 mm, Time 86400 sec |
0.12 % @Thickness 0.125 in, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 3.00 mm |
0.0030 - 0.0040 in/in @Thickness 0.118 in |
|
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0050 cm/cm @Thickness 3.00 mm |
0.0040 - 0.0050 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 67.0 MPa | 9720 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 111 MPa | 16100 psi | ASTM D790 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 35.0 - 40.0 µm/m-°C | 19.4 - 22.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 290 - 310 °C | 554 - 590 °F | |
| Middle Barrel Temperature | 320 - 340 °C | 608 - 644 °F | |
| Front Barrel Temperature | 330 - 350 °C | 626 - 662 °F | |
| Nozzle Temperature | 330 - 350 °C | 626 - 662 °F | |
| Mold Temperature | 110 - 130 °C | 230 - 266 °F | actual surface temp |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 6.00 - 24.0 hour | 6.00 - 24.0 hour | |
| Back Pressure | 0.490 - 1.47 MPa | 71.1 - 213 psi | gage pressure |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N2000NHL Nylon 6 (Cond)
- Kinlead HSS13 Normal Grade Heat Sealable Film (thickness: 30 µm)
- SABIC Innovative Plastics LNP THERMOCOMP AF003 ABS (Asia Pacific)
- SABIC Innovative Plastics NORYL WCD841U PPE-TPE
- Teknor Apex TEKRON® 4300-D90B Thermoplastic Elastomer
- Polyplastics Duracon® TR-5 Acetal Co-polymer (POM), Mineral filling, Mineral filling, High rigidity, Low warpage
- Wellman Wellamid® 22LHI6 XE-N Impact Modified Nylon 66, Lubricated & Heat Stabilized
- EMS-Grivory Grivory® B 70 GFE 30 H PA6-GF30
- Chosun Refractories CJS-1 Joint Sheet
- Bulk Molding Compounds BMC 300 Mineral Filled, Glass Reinforced Polyester
Copyright © lookpolymers.com All Rights Reserved