Zyvex Performance Materials Arovex™ 250 Carbon Nanotube Strengthened Prepreg
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite |
| Manufacturer | Zyvex Performance Materials (ZPM) |
| Trade Name | Arovex™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zyvex Performance Materials Arovex™ 250 Carbon Nanotube Strengthened Prepreg.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Arovex® 250 Prepreg is a 180°F (82°C) to 280°F (138°C) curing carbon nanotube strengthened epoxy prepreg suitable for numerous composites applications. Normal curing takes place at 250°F (121°C). Arovex 250 resin contains an optimum level of carbon nanotubes for additional toughness and enhanced mechanical properties. The carbon nanotubes use molecular dispersion technology to ensure enhancements are evenly distributed throughout the resin. Features: Very high toughnessHigh strengthHigh stiffnessEnhanced mechanical properties Excellent retention of tack and drape
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 0.050 cP @Temperature 120 °C |
0.050 cP @Temperature 248 °F |
Rheology, 2°C/min |
| 0.070 cP @Temperature 80.0 °C |
0.070 cP @Temperature 176 °F |
Rheology, 2°C/min | |
| 1.0 cP @Temperature 40.0 °C |
1.0 cP @Temperature 104 °F |
Rheology, 2°C/min | |
| 100 cP @Temperature 140 °C |
100 cP @Temperature 284 °F |
Rheology, 2°C/min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 46.2 MPa | 6700 psi | 90°; ASTM D3039 |
| 2560 MPa | 371000 psi | 0°; ASTM D3039 | |
| Tensile Modulus | 9.65 GPa | 1400 ksi | 90°; ASTM D3039 |
| 152 GPa | 22000 ksi | 0°; ASTM D3039 | |
| Flexural Strength | 113 MPa | 16400 psi | 90°; ASTM D790 |
| 1830 MPa | 265000 psi | 0°; ASTM D790 | |
| Flexural Modulus | 8.96 GPa | 1300 ksi | 90°; ASTM D790 |
| 176 GPa | 25500 ksi | 0°; ASTM D790 | |
| Compressive Strength | 224 MPa | 32500 psi | 90°; SACMA SRM 1R-94 |
| 1170 MPa | 170000 psi | 0°; SACMA SRM 1R-94 | |
| Compressive Modulus | 10.3 GPa | 1500 ksi | 90°; SACMA SRM 1R-94 |
| 141 GPa | 20400 ksi | 0°; SACMA SRM 1R-94 | |
| Poissons Ratio | 0.34 | 0.34 | ASTM D3039 |
| Shear Strength | 82.7 MPa | 12000 psi | Short Beam; ASTM D2344 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 138 °C | 280 °F | ASTM D702807 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 30.0 min @Temperature 137.8 °C |
0.500 hour @Temperature 280.0 °F |
|
| 120 min @Temperature 121.1 °C |
2.00 hour @Temperature 250.0 °F |
||
| 120 min @Temperature 121 °C |
2.00 hour @Temperature 250 °F |
80 psi | |
| 240 min @Temperature 104.4 °C |
4.00 hour @Temperature 219.9 °F |
||
| 360 min @Temperature 93.3 °C |
6.00 hour @Temperature 200 °F |
||
| 720 min @Temperature 82.2 °C |
12.0 hour @Temperature 180 °F |
||
| Gel Time | 5.00 min @Temperature 137.8 °C |
5.00 min @Temperature 280.0 °F |
|
| 13.0 min @Temperature 121.1 °C |
13.0 min @Temperature 250.0 °F |
||
| 33.0 min @Temperature 104.4 °C |
33.0 min @Temperature 219.9 °F |
||
| 68.0 min @Temperature 93.3 °C |
68.0 min @Temperature 200 °F |
||
| 168 min @Temperature 82.2 °C |
168 min @Temperature 180 °F |
||
| Shelf Life | 12.0 Month @Temperature -17.8 °C |
12.0 Month @Temperature 0.000 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| GIc Strain Release Energy | 3.0 in-lb/in² | ASTM D5528-07 |