Eurotec® Tecomid® NA40 NL XA70 PA6.6, unfilled, flame retardant - halogen free (RoHS compliant), heat stabilized, natural
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Eurotec® Tecomid® NA40 NL XA70 PA6.6, unfilled, flame retardant - halogen free (RoHS compliant), heat stabilized, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Moisture Absorption | 2.00 % <br>@Temperature 23.0 °C |
2.00 % <br>@Temperature 73.4 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 |
| Tensile Modulus | 3.75 GPa | 544 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² <br>@Temperature -30.0 °C |
2.38 ft-lb/in² <br>@Temperature -22.0 °F |
ISO 180/1A |
| 6.00 kJ/m² <br>@Temperature 23.0 °C |
2.86 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75 |
| Vicat Softening Point | 245 °C <br>@Load 5.10 kg |
473 °F <br>@Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | V-0 <br>@Thickness 0.750 mm |
V-0 <br>@Thickness 0.0295 in |
|
| V-0 <br>@Thickness 1.60 mm |
V-0 <br>@Thickness 0.0630 in |
||
| Glow Wire Test | 775 °C <br>@Thickness 2.00 mm |
1430 °F <br>@Thickness 0.0787 in |
GWIT; IEC 60695 |
| 960 °C <br>@Thickness 2.00 mm |
1760 °F <br>@Thickness 0.0787 in |
GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 225 V | 225 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 260 - 280 °C | 500 - 536 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- Plastcom PLASTALEN® PC 69 T 10 003/1M Polypropylene reinforced with mineral filler
- PTS Tristar® PC-10R-CL(15) 15 MFI Clear Polycarbonate with Release
- Lanxess Pocan® T 7331 POS151 000000 PBT + PET, 30% Glass Fiber (discontinued **)
- Industeel SUPERELSO® 690CR Quenched and Tempered High Strength Steel for Leg Components of Jack-up Rigs
- Teknor Apex Telcar® TL-2588L Thermoplastic Elastomer
- Von Roll Isola IMI Varnish 709 Solventless Polyester Varnish for Electrical Insulation
- DuPont™ Kapton® 100EN Polyimide Film, 25 Micron Thickness
- Alliance BCN-11 Bonded (Composite) Magnetic Material
- BASF Polystyrol® 585 K Impact Grade Polystyrene (Europe)
- DuPont Performance Polymers Zytel® HTN 52G35EF BK420 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved