- Lanxess Pocan® TP 740-202 901510 PBT+ASA, 20% Glass Fiber
Lanxess Pocan® TP 740-202 901510 PBT+ASA, 20% Glass Fiber
| Category | Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® TP 740-202 901510 PBT+ASA, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT + ASA, 20% glass fibers, injection molding, low tendency to warp, improved surface finishInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0030 cm/cm | 0.0030 in/in | 60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0070 cm/cm | 0.0070 in/in | 60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1, -2; 5 mm/min |
| Elongation at Break | 2.9 % | 2.9 % | ISO 527-1, -2; 5 mm/min |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 170 MPa @Strain 3.20 % |
24700 psi @Strain 3.20 % |
2 mm/min; ISO 178-A |
| Flexural Modulus | 7.00 GPa | 1020 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| 270 °C | 518 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| 90.0 °C | 194 °F | for test specimens; ISO 294 | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4 - 8 hour | 4 - 8 hour | |
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 7792-1-PBT+ASA, GHMR, 07-070, GF20 |
Users viewing this material also viewed the following:
- MV Labs GD200 GdBr3·xH2O Gadolinium bromide hydrate
- Premix Premi-Glas® 2203-25 CR-SX Fiberglass Reinforced SMC
- Palm Labs Adhesives TURBO FUSE SERIES 130 LOW ODOR/LOW BLOOM (100 Viscosity) Rapid Bonding Adhesive
- Park Electrochemical Nelcote® V-341 Polybutadiene Prepreg, 503 Quartz Reinforced
- Shanghai Ofluorine Z-1 PVDF Injection Grade
- SABIC Innovative Plastics LNP THERMOCOMP 5C003 FP-V (PVDF)
- SABIC Innovative Plastics LNP Thermocomp OFM66 PPS
- Total PS CPDS 855S Chlorine and Bromine Free Flame Retardant High Impact Polystyrene
- Addiplast Addilene H 520 M40 Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved