Ascend Performance Materials Vydyne® 66B, 66J Nylon 66, Dry as Molded

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 66B, 66J Nylon 66, Dry as Molded.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Vydyne® 66B and 66J are members of a family of unreinforced extrusion grade Nylon 66 resins. They are available in natural color. These resins offer high strength, rigidity, and toughness for a broad range of demanding application requirements. Vydyne extrusion grade resins provide good resistance to a wide variety of chemicals, solvents, gasoline, and machine and motor oils. Vydyne 66B Series resins are of high-molecular-weight grade developed to provide high and controlled melt strength. Vydyne 66J Resins are heat-stabilized version for added resistance to elevated temperature use. The high viscosity of Vydyne 66J allows for a very stable and easily controlled melt extrudate. Vydyne 66B and 66J are recognized by Underwriters Laboratories.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ISO 1183
Water Absorption 1.2 %

@Time 86400 sec
 1.2 %

@Time 24.0 hour
 ISO 62
Moisture Absorption at Equilibrium 2.5 %
2.5 %
50% RH; ISO 62
Linear Mold Shrinkage 0.013 cm/cm

@Thickness 2.00 mm
 0.013 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Thickness 2.00 mm
 0.015 in/in

@Thickness 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 82.0 MPa
11900 psi
ISO 527
Elongation at Break 175 %
175 %
ISO 527
Elongation at Yield 10 %
10 %
ISO 527
Tensile Modulus 3.00 GPa
435 ksi
ISO 527
Flexural Strength 34.0 MPa
4930 psi
ISO 178
Flexural Modulus 2.90 GPa
421 ksi
ISO 178
Poissons Ratio 0.42
0.42
ISO 527
Shear Modulus 1.06 GPa
154 ksi
Calculated
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179
Charpy Impact, Notched 0.780 J/cm²

@Temperature -30.0 °C
 3.71 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
0.900 J/cm²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
CTE, linear 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359
Melting Point 260 °C
500 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 66.0 °C
151 °F
ISO 75
Vicat Softening Point 237 °C

@Load 5.10 kg
 459 °F

@Load 11.2 lb
 ISO 306
UL RTI, Electrical 130 °C

@Thickness 0.710 mm
 266 °F

@Thickness 0.0280 in
 UL 746B
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746B
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746B
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 0.710 mm
 167 °F

@Thickness 0.0280 in
 UL 746B
75.0 °C

@Thickness 1.50 mm
 167 °F

@Thickness 0.0591 in
 UL 746B
75.0 °C

@Thickness 3.00 mm
 167 °F

@Thickness 0.118 in
 UL 746B
UL RTI, Mechanical without Impact 85.0 °C

@Thickness 0.710 mm
 185 °F

@Thickness 0.0280 in
 UL 746B
85.0 °C

@Thickness 1.50 mm
 185 °F

@Thickness 0.0591 in
 UL 746B
85.0 °C

@Thickness 3.00 mm
 185 °F

@Thickness 0.118 in
 UL 746B
Flammability, UL94 HB

@Thickness 0.710 mm
 HB

@Thickness 0.0280 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Oxygen Index 28 %
28 %
ASTM D2863
Glow Wire Test 700 °C

@Thickness 3.00 mm
 1290 °F

@Thickness 0.118 in
 Ignition Temperature; IEC 60695-2-12
700 °C

@Thickness 0.710 mm
 1290 °F

@Thickness 0.0280 in
 Ignition Temperature; IEC 60695-2-12
700 °C

@Thickness 1.50 mm
 1290 °F

@Thickness 0.0591 in
 Ignition Temperature; IEC 60695-2-12
850 °C

@Thickness 0.710 mm
 1560 °F

@Thickness 0.0280 in
 Flammability Index; IEC 60695-2-12
850 °C

@Thickness 1.50 mm
 1560 °F

@Thickness 0.0591 in
 Flammability Index; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+15 ohm-cm

@Thickness 3.00 mm
 5.00e+15 ohm-cm

@Thickness 0.118 in
 IEC 60093
Dielectric Strength 14.0 kV/mm

@Thickness 3.00 mm
 356 kV/in

@Thickness 0.118 in
 IEC 60243
Arc Resistance 120 - 180 sec

@Thickness 3.00 mm
 120 - 180 sec

@Thickness 0.118 in
 UL 746A
Comparative Tracking Index >= 600 V

@Thickness 3.00 mm
 >= 600 V

@Thickness 0.118 in
 IEC 60112
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness 0.710 mm
 7.0 - 15 sec

@Thickness 0.0280 in
 UL 746A
15 - 30 sec

@Thickness 1.50 mm
 15 - 30 sec

@Thickness 0.0591 in
 UL 746A
30 - 60 sec

@Thickness 3.00 mm
 30 - 60 sec

@Thickness 0.118 in
 UL 746A
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.710 mm
 >= 120 arcs

@Thickness 0.0280 in
 UL 746A
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 UL 746A
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 UL 746A
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min

@Thickness 3.00 mm
 0.000 - 0.394 in/min

@Thickness 0.118 in
 UL 746A
Processing Properties Metric English Comments
Processing Temperature 250 - 295 °C
482 - 563 °F
Die Temperature 270 - 295 °C
518 - 563 °F
Melt Temperature 270 - 295 °C
518 - 563 °F
Back Pressure 3.00 - 17.0 MPa
435 - 2470 psi