Ravago Manufacturing Americas Hylex® P1007L Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1007L Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength at Break | 69.6 MPa | 10100 psi | ASTM D638 |
| Elongation at Break | 130 % | 130 % | ASTM D638 |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 9.08 J/cm | 17.0 ft-lb/in | 73°F, 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 154 °C | 310 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | 0.0580 in, NA |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.585 | 1.585 | ASTM D542 |
| Haze | 0.50 - 0.80 % | 0.50 - 0.80 % | 125 mil; ASTM D1003 |
| Transmission, Visible | 89 - 91 % | 89 - 91 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.1 kV/mm | 410 kV/in | in Air, 0.125 in; ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 282 - 304 °C | 540 - 580 °F | |
| Middle Barrel Temperature | 288 - 310 °C | 550 - 590 °F | |
| Front Barrel Temperature | 310 - 332 °C | 590 - 630 °F | |
| Nozzle Temperature | 299 - 327 °C | 570 - 620 °F | |
| Melt Temperature | 310 - 338 °C | 590 - 640 °F | |
| Mold Temperature | 82.2 - 110 °C | 180 - 230 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 12 hour | 3 - 12 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Injection Pressure | 10.3 - 13.8 MPa | 1500 - 2000 psi | |
| Back Pressure | 0.483 - 1.03 MPa | 70.0 - 150 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 1000 to 1400 psi |
Users viewing this material also viewed the following:
- Parker Chomerics Waveguide Gaskets 877 Conductive Silicone Elastomer Gasket
- Teknor Apex Monprene® MP 1056 Thermoplastic Elastomer
- SABIC Innovative Plastics NORYL GTX APS430 PPE+PPS (Asia Pacific)
- Zeon Chemicals Sivic® Z702 Polyblend Nitrile Elastomer
- Goodfellow Tungsten 90/Chromium 10 Alloy
- ExxonMobil IPA Isopropyl Alcohol
- Fainplast Compounds GSK 61 Flexible PVC, Injection Molding, Lead Free
- Azdel SuperLite® SL550700-100 PP Resin Matrix / 55% Glass Fiber (1 mm Molded Thickness)
- ATI Allvac® Nickelvac® XM-19 UNS S20910 Specialty Steel
- Bhansali Engineering Abstron HR60N ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved