Solvay Specialty Polymers Ixef® 1032 Polyarylamide (PARA), 60% Glass Fiber (Dry)
| Category | Polymer , Thermoplastic , PVDC , Polyvinyl Dichloride (PVDC) |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Ixef® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Ixef® 1032 Polyarylamide (PARA), 60% Glass Fiber (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ixef® 1032 is a 60% glass-fiber reinforced, general purpose polyarylamide compound which exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; High Flow; High Strength; Low Moisture Absorption; Outstanding Surface Finish; Ultra High StiffnessUses: Automotive Applications; Automotive Electronics; Automotive Interior Parts; Furniture; High Gloss Applications; Metal Replacement; Sporting GoodsInjection Molding Notes: Ixef® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef® resins be dried prior to molding.Additional Properties: Moisture Absorption - Internal Method 1.3 %Automotive Specifications ASTM D6779 PA111G60; BMW GS 93016; GM GM7001M; GM GM7001M PAMXD6 A4 A22 A64 BA661 DC1770 G30 KS2400 MS1800 NS340 RT7 SS225 Color: 0008 Natural; GM GM7001M PAMXD6 A4 A22 A64 BA661 DC1770 G30 KS2400 MS1800 NS340 RT7 SS225 Color: 9008 BlackInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in³ | ISO 1183 |
| Filler Content | 60 % | 60 % | Glass Fiber |
| Water Absorption | 0.13 % @Time 86400 sec |
0.13 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 280 MPa | 40600 psi | ISO 527-2 |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527-2 |
| Tensile Modulus | 24.0 GPa | 3480 ksi | ISO 527-2 |
| Flexural Strength | 400 MPa | 58000 psi | ISO 178 |
| Flexural Modulus | 23.5 GPa | 3410 ksi | ISO 178 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.00 J/cm | 16.9 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C | 7.78 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Unannealed; ISO 75-2/A |
| Flammability, UL94 | HB | HB | |
| Oxygen Index | 25 % | 25 % | ISO 4589-2 |
| Glow Wire Test | 775 °C @Thickness 1.50 mm |
1430 °F @Thickness 0.0591 in |
Glow Wire Flammability Index, IEC 60695-2-12 |
| 775 °C @Thickness 0.800 mm |
1430 °F @Thickness 0.0315 in |
Glow Wire Flammability Index, IEC 60695-2-12 | |
| 800 °C @Thickness 1.50 mm |
1470 °F @Thickness 0.0591 in |
Glow Wire Ignition Temperature; IEC 60695-2-13 | |
| 800 °C @Thickness 0.800 mm |
1470 °F @Thickness 0.0315 in |
Glow Wire Ignition Temperature; IEC 60695-2-13 | |
| 825 °C @Thickness 3.00 mm |
1520 °F @Thickness 0.118 in |
Glow Wire Ignition Temperature; IEC 60695-2-13 | |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
Glow Wire Flammability Index, IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IIEC 60093 |
| Dielectric Constant | 4.5 @Frequency 1.10e+8 Hz |
4.5 @Frequency 1.10e+8 Hz |
IEC 60250 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0090 @Frequency 110 Hz |
0.0090 @Frequency 110 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |
| Middle Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Nozzle Temperature | 260 - 290 °C | 500 - 554 °F | |
| Melt Temperature | 280 °C | 536 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 80.0 °C @Time 43200 sec |
176 °F @Time 12.0 hour |
|
| Moisture Content | <= 0.30 % | <= 0.30 % | |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Hold Pressure | 75.0 MPa | 10900 psi | |
| Back Pressure | 0.000 - 1.00 MPa | 0.000 - 145 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Colors; Natural | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding | |
| RoHS Compliance | RoHS Compliant | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
Users viewing this material also viewed the following:
- Pyrotek RFM Light density refractory composite material
- Fainplast Compounds RK 316 Rigid PVC, Extrusion Lead Free
- Ineos B50-35H-011 HDPE
- Schott GM32087 Dental Glass
- Samyang Trirex® 3025L1 Polycarbonate, Lens Grade
- China Tungsten YGR8 Tungsten Carbide with Rare Earth Additive
- Arlon 51586R035 0.035" (0.889 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Fainplast Compounds AP 93 Flexible PVC, Flame Retardant Insulation
- Lucent Polymers PPC-0222 Polypropylene, Impact Modified
- M. Holland Company MAGMA® LM124-C LLDPE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved