- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Styrolution Novodur® HH-112 ABS
Styrolution Novodur® HH-112 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Novodur® HH-112 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Novodur HH-112 is a high heat injection molding grade. It provides good heat resistance combined with enhanced stiffness.Information provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.25 % @Temperature 23.0 °C |
0.25 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 114 MPa | 16500 psi | ISO 2039-1 |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | ISO 527 |
| Elongation at Yield | 3.1 % | 3.1 % | ISO 527 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527 |
| Flexural Strength | 81.0 MPa | 11700 psi | ISO 178 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ISO 178 |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 14.0 J/cm² @Temperature 23.0 °C |
66.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 109 °C | 228 °F | ISO 75 |
| Vicat Softening Point | 112 °C @Load 5.10 kg |
234 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 118 °C @Load 1.02 kg |
244 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Strength | 41.0 kV/mm @Thickness 1.50 mm |
1040 kV/in @Thickness 0.0591 in |
Short Time; IEC 60243-1 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 270 °C | 446 - 518 °F | ISO 294 |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- LNP Lubricomp® UFL-4036 HS Polyphthalamide, Glass Fiber Reinforced, PTFE Lubricant (discontinued **)
- Indium Corp. WF-7742 VOC-Free Wave Solder Flux
- Samsung Cheil Industries Starex® WX-9700 ASA, Unreinforced Extrusion Grade
- Formosa Plastics Formolon® 25 PVC
- Master Bond Supreme 10HTFS Silver Conductive Microelectronic Epoxy
- Azoty Tarnow™ Tarnamid® T-27 CF20 Polyamide 6 20% Carbon Fiber- Antistatic and Electroconductive
- 3M AC-236 Class C-20 Aerospace Sealant
- Bhansali Engineering Abstron SHF-50+ ABS Injection Molding Grade
- 3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive
- Termopol Termoton® K2GA4055D TPE Compound, based on SEBS and Polyolefins
Copyright © lookpolymers.com All Rights Reserved