DuPont Performance Polymers Delrin® FG100AL NC010 Acetal Homopolymer (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® FG100AL NC010 Acetal Homopolymer (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Delrin® FG100AL is a high viscosity, lubricated acetal homopolymer resin, containing an advanced system of lubrication. It has been developed for consideration into applications such as parts for the food industry.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.020 cm/cm @Thickness 2.00 mm	0.020 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Thickness 2.00 mm	0.018 in/in @Thickness 0.0787 in	ISO 294-4
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Melt Index of Compound	1.7 g/10 min @Load 2.16 kg, Temperature 190 °C	1.7 g/10 min @Load 4.76 lb, Temperature 374 °F	cm3/10 min; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	70.0 MPa @Temperature 23.0 °C	10200 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	45 % @Temperature 23.0 °C	45 % @Temperature 73.4 °F	nominal; ISO 527
Elongation at Yield	18 % @Temperature 23.0 °C	18 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	3.00 GPa @Temperature 23.0 °C	435 ksi @Temperature 73.4 °F	ISO 527
Flexural Modulus	2.80 GPa @Temperature 23.0 °C	406 ksi @Temperature 73.4 °F	ISO 178
Charpy Impact Unnotched	17.0 J/cm² @Temperature -30.0 °C	80.9 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	25.0 J/cm² @Temperature 23.0 °C	119 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.900 J/cm² @Temperature 23.0 °C	4.28 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	500 µm/m-°C @Temperature -40.0 - 23.0 °C	278 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 23.0 - 55.0 °C	278 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 55.0 - 100 °C	278 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C @Temperature -40.0 - 23.0 °C	55.6 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	110 µm/m-°C @Temperature 23.0 - 55.0 °C	61.1 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	150 µm/m-°C @Temperature 55.0 - 100 °C	83.3 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	163 °C	325 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	97.0 °C	207 °F	ISO 75-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	215 °C	419 °F	Optimum; Injection Molding
	210 - 220 °C	410 - 428 °F	Injection Molding
Mold Temperature	90.0 °C	194 °F	optimum; Injection Molding
	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.20 %	<= 0.20 %	Injection Molding

Descriptive Properties	Value	Comments
Appearance	Natural Color
Features	Creep Resistance, Good
	Friction, Low
	Homopolymer
	Impact Resistance, Good
	Lubricated
	Viscosity, High
	Wear Resistance, Good
Forms	Pellets
Generic	Acetal (POM) Homopolymer
Material Status	Preliminary Data
Part Marking Code	>POM-S<	ISO 11469
Processing Method	Injection Molding
Product Category	Food Contact Resins
	Low Wear and Friction Resins
	Unreinforced Resins
Region Available - Global	Yes
Resin Identification	POM-S	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Conveyors
	Food Applications, Non-specific
	Gears
	Parts, Engineering